Electronics Forum | Thu Jul 15 14:55:24 EDT 1999 | JohnW
| I'm designing a board where the parts will only fit if I do one of the following: | | 1. Put BGAs on both sides | | 2. Put BGAs on top, smt TSOPs directly underneath and using blind vias to keep the real estate on the bottom side below the BGA pa
Electronics Forum | Mon May 16 16:40:50 EDT 2005 | russ
Fred, give us a quickie at what you will be soldering Single sided thu hole, double sided SMT, both, lead pitches and protrusions, Flux type, and such. Buying a used wave can be tricky and the more info up front the better we will be able to tell yo
Electronics Forum | Thu Nov 13 12:49:45 EST 2014 | dyoungquist
I have no experience running a "move the board" selective solder so can not compare the 2 methods..... We have been using an RPS Rhythm "move the pot/nozzle" system since 2008. We are using it solder thru hole components onto boards that often have
Electronics Forum | Fri Jul 26 05:14:38 EDT 2013 | anilw2006
We had a solder joint problem in gold plated PLCC68 ic. We do double sided reflow process with Cookson OL107F paste. First we do top with paste and second with glue process.The solder joint shape and wetting looked normal.In the process of testing
Electronics Forum | Mon Jun 12 06:45:10 EDT 2000 | kim ji tae
Hi! Thanks all who upgrade these pages. I have some questions. Is there any answer? I do double-sided reflow solderig, with 0.4% AG solder cream. with AU finished pcb. First I do reflow solder bottom side where 0.5pitch TQFP locates. Second I do re
Electronics Forum | Tue May 17 09:58:42 EDT 2005 | Fred N
Thx to everyone who replied. we will be running single sided thru hole and double sided smt, 186 rosin flux cause they tell me it can take the heat needed for 18 layer pwbs. some long leads. also they are ordering in pallets to deal with the irregu
Electronics Forum | Mon Jan 26 11:46:16 EST 1998 | Rin Or
| I have a problem! The solder on my pc boards look great comeing out | of my reflow oven. They go thrue the rest of the prossese | and at the end at the qc station it's cold or whitish or gray not shiny. | does any one have a idea on how to correct
Electronics Forum | Wed Feb 12 13:37:22 EST 2003 | dwanzek
I need some input on what good solder thieves dimensions should be. I am limited to solving my bridging problem with solder thieves; all process/wave variables have been adjusted to try to solve this problem. There are several of these connectors on
Electronics Forum | Mon Apr 12 15:52:12 EDT 2004 | wgaffubar
I am using Indium 92J type 4 solder paste due to a BGA site with .008" pads and stencil opening of .009" square and .005" stencil thickness. When I try the type 3 we get insuffecient print. The aspect ratio tells me that I should be using a type 4. T
Electronics Forum | Tue Dec 14 11:13:43 EST 1999 | Chris May
Paul, I have (as many have) come across this problem due to misregistration of resist at the PCB fab. You didn't say if these boards are inexpensive double sided or costly multis. I know this shouldn't make a difference on quality but I would tend t
.gif)