Electronics Forum | Wed Dec 20 04:43:36 EST 2006 | greg york
Any decent flux would volatise off with the heat of the wave unless absorbed into the solder mask. Test this by trying to clean in alcohol or common solvent aerosol, if it does not clean then it is probably Mineral Salts from solder mask fillers. Ano
Electronics Forum | Wed May 07 10:15:46 EDT 2008 | llaerum
We are also having some issues with certain small parts. In our case this is tantalum caps and 0402 caps. We had a vendor admit after much discussion that the plating used from a particular orgin was different on the tantalums. The tehory is thatthsi
Electronics Forum | Tue Aug 12 14:49:26 EDT 2008 | awegener
I'm attempting to pick and place a small rivet onto our PCB. The rivet should be attached via reflow solder. The rivet will be used to create a sandwich, holding together a frame and additional circuit board in a package. This part is intended onl
Electronics Forum | Thu Oct 01 13:33:01 EDT 2015 | marlyn
Hey there fellow people with SMT > issues... What's the proper procedure for > soldering through-hole headers on the back-side > of the PCB (pins poking out on same side as SMT > parts)? ( Yes - I did the SMT side first and am > now faced with L
Electronics Forum | Mon Feb 19 11:25:07 EST 2001 | markt
I am currently cleaning solder paste and adhesive stencils and misprinted substrates manually by using IPA, chem wipes, Q-tips, etc. Can you recommend a machine and chemistry that will clean all these applications?
Electronics Forum | Tue Jun 05 16:40:46 EDT 2001 | kerryn
Thanks Phil. However, my objective is to identify stencils that are not 100% clean prior to sending to inventory. I want to catch it before the solder paste has a chance to dry and harden in the apertures. Kerry
Electronics Forum | Fri Jul 16 15:30:22 EDT 1999 | SMTASSY
Perhaps a little hard to find but is there anyone who uses a vapor phase process to solder populated card with BGAs. I am interested in the success rate of such a process. It is obvious that the throughput is reduce vs a convection oven but still thi
Electronics Forum | Tue Sep 18 11:34:36 EDT 2001 | jschake
The tightest spacing between neighboring 0201 components assembled was 8-mils. Please refer to the response for the query entitled �Minimizing Tombstoning Defects� posted by martys, as the response provided there is also relevant to address this que
Electronics Forum | Wed Oct 23 08:40:20 EDT 2002 | davef
Yer not making this easy. What kind of flux? If no-clean flux, what controls are you using to assure you are: * Applying the correct amount of flux? * Properly activating the flux? If water washable flux, talk to us about your cleaning methods and
Electronics Forum | Thu Oct 24 15:02:16 EDT 2002 | seand
Hello Yannick, Have you brought this concern up with your supplier? I would recommend speaking with your flux and paste provider to gain additional insight and recommendations for resolving the concern. Good luck, Sean D.