Electronics Forum | Wed Apr 14 13:39:48 EDT 2004 | procon
Also check out AIM's NC368 / LF218 www.aimsolder.com
Electronics Forum | Thu Apr 15 15:32:27 EDT 2004 | russ
Where does the 260 Deg. C spec. come from that you mention?
Electronics Forum | Wed Apr 14 12:23:59 EDT 2004 | Ted
Hi everyone! I am looking for a lead-free solder that will survive a customer reflow of 260C. I am currently using SN10/Pb88/Ag02 but the reflow temperature is to high (320C) for the FR4 boards that we have. I know there are higher temp FR4 boards
Electronics Forum | Thu Jul 20 17:35:23 EDT 2000 | joevo2k
Bob, Is Nitrogen a "MUST" for reflow and wave soldering of the Lead-Free Solder Alloys ? And is post cleaning be a great impact when converting to Lead-Free Solders ?
Electronics Forum | Sun Nov 27 05:04:02 EST 2016 | pmcg
Never used stainless pots as when we converted to lead free we changed all the pots to titanium. Been using SN100C for many years now, very good results, also use it in reel form in our selective solder machines with great results. Bear in mind the
Electronics Forum | Wed Oct 01 10:01:15 EDT 2008 | davef
We've never used the 99*C lead-free solder you mention. We have used a leaded solder that can form a 93*C eutectic solder. So, we had to be sure the service temperature [of the solder connections] as below 80*C.
Electronics Forum | Thu Jul 20 16:14:59 EDT 2000 | Cole
How effective will current wave solder equipment and processes be with lead free solder? What temperatures will be required? How will dross generation compare?
Electronics Forum | Thu Apr 15 14:36:06 EDT 2004 | Ted
I need solder that has a solidus temp. of approximately 260C so that when sent through a second reflow of 260C the solder doesn�t become liquidus. However, I need the max reflow to be less that 300C because of the substrate.
Electronics Forum | Mon Sep 29 10:04:40 EDT 2008 | illheader
Has anyone used lead free 99C bar solder/paste? Looking for more information other than what the manufacturers give you. Thanks
Electronics Forum | Fri Jun 12 07:14:36 EDT 2015 | gabinocf
Thanks by your response, at this moment I have problems in a Lead Free process the issues that i have are solder peaks, by my understanding this conditions is due to lack of flux, bad temperature profile or the dwell time is too long. My concern is,
winsouce.jpg)