Electronics Forum | Wed May 09 17:26:57 EDT 2001 | davef
Awww, don beso tuff on ursef!!! It sounds like you�re thinking correctly with what you�ve done, but it�s possible that the test you ran did not represent your actual production environment as well as you would have liked. So, you just need to "cran
Electronics Forum | Fri Jun 27 10:27:59 EDT 2003 | davef
Since you�re asking the question about proper handling of OSP board, there may still be time to talk you out of using that material. * Cleaning of mis-printed board could cause non-wetting problems. This tends to remove a fraction of OSP coating. 0.3
Electronics Forum | Thu Mar 11 16:44:34 EST 1999 | Earl Moon
| | For Dean and the rest of you interested, | | | | I have reconciled many of my thermal issues with this machine and its peculiarities. The bottom side heater seems adequate, at 750 watts (not going to spend 10 grand extra for 500 more watts no ma
Electronics Forum | Wed Oct 03 23:58:23 EDT 2018 | gaintstar
Flason SMT News: http://www.flason-smt.com/new/6-Things-to-Check-Before-Submitting-Your-PCB-Design-for-Manufacturing.html http://www.flason-smt.com/new/about-wave-soldering-machine-tin-pot.html http://www.flason-smt.com/new/Advantages-of-Design-for-
Electronics Forum | Sat Sep 18 13:05:57 EDT 1999 | Brian
| | | | | | Dave, I'll respond by paragraph: | | | | | | | Brian: | | | | | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like habanero slath
Electronics Forum | Sat Sep 18 14:37:00 EDT 1999 | Earl Moon
| | | | | | | | | Dave, I'll respond by paragraph: | | | | | | | | | Brian: | | | | | | | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like