SolderTips: Dealing with the Problems of Soldering Iron Tips Breaking Down | EPTAC

| https://www.eptac.com/soldertips/dealing-with-the-problems-of-soldering-iron-tips-breaking-down/

. We are soldering lead free materials between 600 and 700 degrees F and increasing the contact dwell time by about 1 to 1.5 seconds. The new lead free alloys are high in tin content and the tin will dissolve the plating on the solder iron tip and eventually eat through the tip

SolderTips: Dealing with the Problems of Soldering Iron Tips Breaking Down - EPTAC - Train. Work Sma

| https://www.eptac.com/soldertip/soldertips-dealing-with-the-problems-of-soldering-iron-tips-breaking-down/

. We are soldering lead free materials between 600 and 700 degrees F and increasing the contact dwell time by about 1 to 1.5 seconds. The new lead free alloys are high in tin content and the tin will dissolve the plating on the solder iron tip and eventually eat through the tip

SolderTips: Dealing with the Problems of Soldering Iron Tips Breaking Down - EPTAC - Train. Work Sma

| https://www.eptac.com/faqs/soldertips/soldertip/soldertips-dealing-with-the-problems-of-soldering-iron-tips-breaking-down

. We are soldering lead free materials between 600 and 700 degrees F and increasing the contact dwell time by about 1 to 1.5 seconds. The new lead free alloys are high in tin content and the tin will dissolve the plating on the solder iron tip and eventually eat through the tip

Solder Products : Frequently Asked Questions | Nordson EFD

ASYMTEK Products | Nordson Electronics Solutions | https://www.nordson.com/en/divisions/efd/resource-center/solder-frequently-asked-questions

? Recommended storage temperature for solder paste is between 40°F and 50°F (4°C to 10°C). Storage at temperatures above refrigeration will reduce shelf life and voids the guarantee

ASYMTEK Products | Nordson Electronics Solutions

. J-STD-001Changes Between Revisions of Docs 6 Why Gold Plating Pro •  Gold: –  Does not tarnish –  Does not oxidized –  Is solderable –  Has a long shelf life Con

| https://www.eptac.com/wp-content/uploads/2012/09/eptac_10_17_12.pdf

: –  oxidation of the tip plating – Use of very small solder wire. •  Solder will ball up on a dewetted tip •  Heat transfer is also impacted with a dewetted tip 7 Tip Care Practices To Prevent and Reduce Dewetting

| https://www.eptac.com/wp-content/uploads/2014/11/eptac_11_19_14.pdf

•  Gold: – Does not tarnish – Does not oxidized –  Is solderable – Has a long shelf life Con •  Gold: –  Porous –  Can be too thick – Dissolves in Eutectic Tin/Lead

| https://www.eptac.com/wp-content/uploads/2016/05/eptac_06_22_16.pdf

TRC Circuits

| http://www.thebranfordgroup.com/dnn3/Employees/OnlineAuctionAdmin/TRCCircuits/tabid/1902/AuctionID/1636/Default.aspx?page=2

: The Lots will have a staggered closing time with 2 closing every minute in numerical order. For Example: Lots 1 and 2 will start to close at 10

Ask Questions | EPTAC

| https://www.eptac.com/ask/

: I see so many places say that they build to IPC-A-610, yet I thought you build to J-STD-001, and inspect to IPC-A-610. Is this correct? Read Answer Shelf Life of Soldered Components Question

ezCLIP

| https://pcbasupplies.com/automation-tooling/ezclip/

ezCLIP is manufactured from high quality spring steel and coated for long life use. Installation is simple; just push the clip over the PCB magazine rack slot that needs to be skipped. The bright finish is a visual cue that the card guide slot is not