Electronics Forum | Sat Nov 13 14:09:45 EST 1999 | se
First, let me say what I always say: a good chem-etched stencil will print fine pitch. Chem-etch brings trap to the side walls because its a physical by-product of the process. Because they are less expensive you can add electropolish and still save
Electronics Forum | Thu Jun 27 21:28:42 EDT 2002 | davef
You're correct that the Ni/Pd termination seems to have something to do with you solder balling. It could be related to the interaction between your paste and the Pd. I assume these are really 'fines' rather than 'balls'. Things that come to mind a
Electronics Forum | Wed Jun 21 19:01:48 EDT 2017 | mac5
Try baking the boards; you may have a moisture problem.
Electronics Forum | Fri Feb 19 14:43:46 EST 1999 | Nithy
We are in the process of getting into no-clean paste and fluxes. One important issue in this is sodler balling. I have heard some people say that having a matte finish would help in having lesser solder balls and that the solder balls would not be
Electronics Forum | Fri Jan 28 01:56:32 EST 2005 | Chua
Hi, I could like to find out what are the things need to look out if I'm doing a new SMT solder paste ( water soluble & no-clean ) evaluation. And also flux ( spray type ) for wave-solder ( water soluble & no-clean ). Appreciate for all the input..
Electronics Forum | Mon Dec 17 15:41:15 EST 2007 | shrek
Ha-ha-ha-ha-ha,me lad. Wave solder is like an onion, it's got many many layers. Kind of like me-self. I'm a big ogre with many complex layers. At any rate i like the other colleague with his adverstising trigger finger. by golly, me chap, he's a
Electronics Forum | Thu Jun 27 11:22:03 EDT 2002 | robbied
Hi there. We have had an out of control reflow oven that has allowed its temperature to fluctuate by up to +/- 20 deg C from set point in very short periods of time. We found the root cause of the problem and fixed it, but by then we had already run
Electronics Forum | Tue Jun 20 15:08:30 EDT 2017 | ranap121212
Hello I have the problem with selective soldering on the robot. Thin balls appear on the laminate. The tin sometimes shoots...? and then the balls are a few millimeters from the soldering point. I tried up or down with temperature, but it did not wor
Electronics Forum | Mon Dec 17 11:55:08 EST 2007 | chef
I recently had the same problems, solder bridges on every thing I made, different customers boards, etc. I wave with no-clean flux. As I sorted out problems (pin holes, blow holes, splatter, etc.) I found a lot of variable factors. I changed flux,
Electronics Forum | Fri Apr 20 16:05:17 EDT 2001 | gcs
We always reduce side to side, EXAMPLE: 12 mil width reduced to .010". Do you guys check viscosity ? Also maybe your guys are appling to much pressure on the sqweegee blades.
.gif)