Electronics Forum | Sat Nov 26 05:55:04 EST 2005 | milroyperera
Hi, Does any body have the experience with wave soldering a "Gold" plated PCB with SMD assembled on it? I`m experiencing massive bridging,icicles,Shadowing & Skipping. The present soldering angle is 6 deg:,pre heating rate is 2 deg/sec , Dwell time
Electronics Forum | Mon Nov 28 09:46:24 EST 2005 | pjc
I have waved gold (ENIG) boards. That's a pretty hot pot at 260C, wow. I have used 245C with good results. All other parameters look OK a glance. Well, PCB temp looks a little hot too at 130C before pot. 90-100C is typical for most No-Clean flux. At
Electronics Forum | Thu Mar 30 09:32:54 EST 2006 | russ
Not arguing dan, but are you positive that they are not copper? anyway, what is happening is as the parts sucks down onto the board from reflow the extra paste is notnecessarily sqeezed out but it has no place to go. So it will form this ball on th
Electronics Forum | Thu Mar 30 10:21:44 EST 2006 | Dan
Sorry about that(My bad), they are copper. I believe the same thing, we need to reduce the appatures as we are already at 5mil. Our main problem is the customer...Their tests were failing and for some reason they touched that part up, and then the un
Electronics Forum | Thu Apr 15 11:14:34 EDT 2004 | mikecollier
Our conformal coat area has recently requested changes to our bare board houses to perform a pumice scrub operation on the PWB prior to HASL plating and delivery to us. Our first lot received caused us to have void faults under multiple component ty
Electronics Forum | Wed Oct 24 18:08:02 EDT 2001 | davef
1- DF1: WOW!!! How do people get these cool toys? CB: I am with the University at Buffalo Electronic Packaging Lab. http://www.packaging.buffalo.edu We have pretty much everything that is sold on the market as well as Laser inspection technologies we
Electronics Forum | Thu Aug 26 10:28:07 EDT 1999 | Stuart Adams
What are the key steps to achieving high yield with CSP ??? (We are trying qualify vendors for volume fab/assembly of some products which use several CSP devices on each side of the board. (Some with 0.5mm ball pitch)) Looking through the forum I
Electronics Forum | Thu Oct 25 16:48:29 EDT 2001 | Cemal Basaran
We can inspect and measure strain field in anything larger than 320nm with Laser techniques we have. We can do this measurements during fatigue testing. Of course thick intermetallic region as a solid region is a problem due to the fact that you ha
Electronics Forum | Thu Oct 18 18:37:49 EDT 2001 | davef
You�re correct. Probably every supplier�s product has slightly different cure characteristics. Let me spin this up a little differently � There was a slight imbroglio in my office this morning involving a couple of stalwarts and the last Krispy Kr
Electronics Forum | Thu Jun 28 10:46:44 EDT 2001 | genny
Thank you. I'm sorry if I came across frustrated or anything, but I wasn't sure if people were ignoring the one question I kept asking or if, as you said, they just didn't know. Here's the deal. We are a small company rapidly growing into a larger