Electronics Forum | Tue Sep 21 13:10:10 EDT 1999 | Dave F
| Dear All, | | In order to understand the soldering technologies in SMT, I'd like to understand why some cards are soldered and then cleaned, or only soldered whitout water cleaning nor "ultra sound" wavelength. | | I mean that I wonder why we use
Electronics Forum | Fri Jan 29 05:14:06 EST 1999 | Graham Naisbitt
Hi guys, I really am at a loss to understand this one. It would appear that there may be some reaction between the flux and the resist? Or maybe you have an OSP on the board that is reacting during soldering? As a fast fix, maybe you should try a
Electronics Forum | Tue Jun 09 15:46:29 EDT 1998 | Aric Parr
| Hi there Gary, | Your solder ball problem is very similar the problem I experienced, but I was using a water soluble paste at the time. It started by inspectors telling me that they were seeing cold solder on some SIMM's that we had built regularly
Electronics Forum | Mon Aug 09 14:58:33 EDT 1999 | Earl Moon
| | Earl, why don't you post this ALSO in the "Mart". Is there a reason? | | | | | | | | | | | Folks, | | | | | | | | | | Probably not the forum, but forgive me as I am but a dog as described by Justin and admitted by me. However, I am looking fo
Electronics Forum | Thu Sep 17 11:09:32 EDT 1998 | Dave F
| I need an evaluation process to prove to a customer that our no-clean process does not leave excessive residue? Any ideas? Wayne: More of the same as Chry and Justin. KEY ISSUE The first thing that you need to know is: What does your customer me
Electronics Forum | Thu Sep 17 12:00:19 EDT 1998 | Mike C
| | I need an evaluation process to prove to a customer that our no-clean process does not leave excessive residue? Any ideas? | Wayne: More of the same as Chry and Justin. | KEY ISSUE | The first thing that you need to know is: What does your cus
Electronics Forum | Mon Jun 28 10:03:22 EDT 2004 | davef
First, welcome to your new job. Second, IPC-TM-650 2.6.14 is only loosely an �Ionic Contamination (Electromigration) Test�. * Electromigration Test, IPC TM 650 2.6.14, 2.6.14.1 * Ion Chromatography for Ionic Cleanliness, IPC TM 650 2.3.28 Third, I
Electronics Forum | Mon Jan 08 20:57:52 EST 2001 | Dave F
Are you talking about bare board cleanliness or assembly level cleanliness? Bare board cleanliness is still primarily measured by resistivity of solvent extract (ROSE) using instruments such as Omegameters and Zero Ions. What is considered as "acce
Electronics Forum | Mon Nov 29 11:37:51 EST 1999 | cpitarys
Hello Jason, I will look for the best price and service support to start. Also request an in house trial at the vendor. Jason, are you looking to remove a no clean paste or water soluble paste? Single Chamber Equipment: Most stencil cleaners opera
Electronics Forum | Sat Jan 16 03:06:36 EST 1999 | Wirat S.
| | Our spec on voids is 30% ball diameter in the center. On the component to ball and pad to ball interface, we use 25%. To determine this spec, we asked around. I don't know of any studies that have been done to verify if this is OK | | | | Regard