Electronics Forum | Thu Dec 15 17:30:42 EST 2005 | GS
Yes Davef, storage condition and long time remaining on shelf could effect pealing strength, but we experimented that by using Polystirene Carrier Tape also this problem was reduced almost to zero. Df, If I am not wrong when you talk about pr
Electronics Forum | Thu Dec 15 19:43:33 EST 2005 | Liza
Stefan - We are using an automatic sealing equipment and have several controls also. The particular machines used for processing these products could be narrowed down to 5 machines at most. The sealing temp, pressure and dwell time are checked on a
Electronics Forum | Fri Dec 16 10:25:14 EST 2005 | GS
Hi Liza - polystirene monolayer (blend ?) could be sealed at less presure, ie 35-40 PSI. Temprature could be 165�-170�C. For sure after sealed you shoud make sure the sealing strength (peel strength)should meet min 15-25 N.(bet avg from 25 to 45 N)
Electronics Forum | Sat Dec 17 13:58:25 EST 2005 | bvdb
Jared, Thank you for the help. AFter following your advice we were able to get the display to say Jog L. However, pressing the UP or DOWN arrow or pressing the "F" key and the UP or DOWN arrow didn't do anything. The trays stay put. When we requ
Electronics Forum | Thu Dec 15 23:04:07 EST 2005 | Manyhats
Hello, we are a low volume high mixed CM looking for a new addition to our SMT depot. We are currently running 2 Mydata TP-11 Hydra and feel that this can not meet our 06' forcast and current builds. I need to make a decision whether to go with the S
Electronics Forum | Wed Dec 21 10:00:28 EST 2005 | russ
I'm curious about the "large infrastructure" statement. Do you or anyone believe that the large infrastructure is better? Sometimes, I am not so sure. I actually rate Dynatechs service as some of the best I have had. (No, I do not work for Dynatec
Electronics Forum | Wed Dec 21 11:13:28 EST 2005 | rlackey
Hi Rick, That is one theory and although valid is probably not something I'd go with. There are 2 ways of going for a new market - a) Carpet bomb it, by throwing huge resources into it and hoping to catch everything. b) Starting in one area/stat
Electronics Forum | Thu Jan 26 13:12:19 EST 2006 | Erik
We just bought a SM320 an will receive it next week. We had 3 days of user training this week and from my point of view it is a very good machine. Really easy to use and very fast and accurate. On our testboards we achieved *realistic* speeds of 10.0
Electronics Forum | Thu Jan 26 16:21:04 EST 2006 | robls
We are a contract manufacturer in South Africa and have been running with Samsung equipment since 1999. To date we have 8 machines running 18 hours a day and have had nothing but fantastic service from these machines. We started with the old CP30 mac
Electronics Forum | Fri Dec 16 03:47:46 EST 2005 | gpaelmo
Anyone have problems wave soldering white tin finish? We are an ems and our customer provides us the pcb's. SMT and TH components on the board. SMT is fine but when we wave solder, wetting to top side is very poor (solder only flows half way up). We