Electronics Forum | Mon Oct 16 20:50:34 EDT 2000 | Dave F
This is vague. What is causing ... When does it appear ... What is it's occurance ... What is the frquency ... What does it look ... What problems does it ... And on and ...
Electronics Forum | Thu Sep 21 12:10:16 EDT 2000 | Boca
On the money as usual! (Your subtle approach is something to behold. Much like my approach, which has gotten me into more grief over the years than I should be allowed to have.) Boca
Electronics Forum | Wed May 10 16:49:14 EDT 2000 | Michael Parker
I would like informnation regarding this high heat withstanding type material for PCB, also any other types that are compatible. We currently use FR4 but have an application that may require most advanced composition.
Electronics Forum | Thu Jan 20 10:16:27 EST 2000 | Neil
After some serious digging I have found and fixed the error that kept anyone who didn't accept cookies from getting their email. Everone should be able to access their email now. Thanks for your patience. Neil
Electronics Forum | Mon Jan 10 16:58:50 EST 2000 | Brian E. Steelglove
I am trying to edit my company mini-page. Please call me with the details. Brian E. Steelglove 847-288-4487
Electronics Forum | Fri Dec 10 16:32:55 EST 1999 | John Thorup
well... it depends on what you are placing. Many odd-form placement machines, like Chad or Jot, use some sort of mechanical gripper as a "nozzle" without vacuum. John Thorup
Electronics Forum | Mon Nov 01 10:16:42 EST 1999 | Mark Anderson
I am interested in getting some feedback on what different companies are doing to eliminate the solder beading issues on 0603, 0402 chip components using a no-clean process. We are currently incorporating a solder mask removal between the solder lan
Electronics Forum | Sat Oct 16 05:07:03 EDT 1999 | Brian
I'd have put it myself into the Admin group, but I wasn't able to :-( However, it must have been a fluke: yesterday afternoon and this morning, it was back to its usual snail's pace : 2,8 kb/s today. Pity! Brian
Electronics Forum | Mon May 10 16:51:32 EDT 1999 | Ruby Zheng
| Can anyone tell me what the recommended material for molding with thermal expension coeffecient around 20ppm and transparent for lightwave 850nm. Thanks |
Electronics Forum | Wed Mar 10 16:18:29 EST 1999 | greg cronin
I am looking for a supplier for bare fr4 material. I use the fr4 for fixtures and my supply has run out. A supplier in the new england area would be the best. thank you
winsouce.jpg)
.gif)