Electronics Forum | Thu Aug 03 19:49:16 EDT 2000 | Darby
I presume you have no vision alignment. Buy yourself a little monocular measuring microscope ( about $100 ). You are not going to get the registration you require between stencil and pcb for each print if you are running off tooling pins , edge clamp
Electronics Forum | Mon Oct 11 15:06:39 EDT 1999 | Dave F
| | Thank you all for your replies. I guess my age in this industry is showing. This military spec. does not appear to be in existance. So, let me make my request a little more to the point: | | | | Is anyone aware of a specification specifically
Electronics Forum | Mon Aug 31 16:23:37 EDT 1998 | Bill Boles
We have an unusual problem here and I'm reaching for more input if anyone can help??? We are an OEM manufacturer of PCA's. After a history of consistent quality designs, we have one small memory SIMM that is causing major headaches for us and our PCB
Electronics Forum | Mon Feb 25 21:09:48 EST 2002 | davef
You are correct about a TCE [CTE] mismatch issues in ceramic packages. The coefficient of thermal expansion [ppm/�C] of major ceramic package elements are: * Silicon - 3 * Standard 92% alumina ceramic � 6.5 * FR4 board � 18-20 Several points are: *
Electronics Forum | Tue Jul 02 02:50:55 EDT 2002 | ianchan
Hi mates, was going thru the IPC-A-610C Standards, and noted BGA voids stands somewhere between 10%-25% voids permissible in the solder "ball" bump, after reflow process. Was wondering, hypothetical case study, is there any specification for voids
Electronics Forum | Sun Mar 26 19:02:05 EST 2006 | ms
Hi We are running automatic stencil printers, open squeegees, stainless stencil, stainless blades, print speed 25-30mm/sec. We have a frustrating consistency issue printing .37x.3mm apertures on a 45pin LGA (11 pads each side, 1 large ground in mid
Electronics Forum | Tue Oct 28 06:18:19 EDT 2008 | dominikpeli
Dear Collegs! I would appreciate all responses with opinions about the AOI manufacturers that will be listed below. First of all maybe a short description. In my company we are just starting with the optical inspection of our products. We use screen
Electronics Forum | Fri Aug 01 18:50:02 EDT 2014 | hegemon
There are no BGA rework stations in that price range that I would consider for purchase. (or did you miss a zero in your cost estimate?) In order to have placement, and sufficient heating for proper BGA rework (top and bottomside)you're going to hav
Electronics Forum | Mon Mar 01 22:24:53 EST 1999 | Dave F
| It seems to be that we have to much NaCl left on our assambled PCB's. | The flux we use is from cobar. They say it can not be from the flux... So what can be the reason, what kind of problem may occer when there is to much NaCl. | George: When so
Electronics Forum | Thu Sep 03 12:36:11 EDT 1998 | davef
| We have an unusual problem here and I'm reaching for more input if anyone can help??? We are an OEM manufacturer of PCA's. After a history of consistent quality designs, we have one small memory SIMM that is causing major headaches for us and our P