Electronics Forum | Mon Mar 24 16:49:42 EDT 2008 | paulv
Fellows, First of all, thank you for taking the time to respond to the post, however some of you missunderstood the main objective of it. I was basically trying to find historical and current average market prices for solder products. Metal informati
Electronics Forum | Thu Jul 31 13:42:08 EDT 2008 | comatose
I'm looking to fill a solder fountain with 50lb of SN100C. My usual source for paste and the like doesn't stock this alloy. We run double sided reflow, so we're not going to be needing hundreds of pounds for a wave machine at any point. Who is the
Electronics Forum | Thu Oct 02 03:11:42 EDT 2008 | gsala
Ask FELDER (gmbh), they can replace the alloy (SN100 +Ge+Ni ...) or even with a special kit (FUJI Patent) or if preferred you can transform the solder in the pot w/out replace it in a reliable way. http://www.felder.de/en_produkte.phtml Regards...
Electronics Forum | Fri Nov 02 09:09:56 EDT 2012 | davef
Sure you can use it it with leaded HASL. Recognize that ... * Your Sn42/Bi58 will no linger be Sn42/Bi58 * Your leaded HASL will no longer be the same leaded HASL that walked in the door to your plant * Lead from HASL coatings can diffuse through the
Electronics Forum | Wed Aug 30 16:00:42 EDT 2000 | Dave F
Russells: You can mix the two solders you mentioned, assuming by "96s" you meant "96Sn / 4Pb". If you heat the two tin / lead alloys to a liquid state, you�ll form a tin / lead solution with properties different from either of the two solders. The
Electronics Forum | Tue Jan 10 14:44:42 EST 2006 | greg york
Not sure about Sn/Cu/Ni large market share here in Europe as we have a large part of the UK market with SACP0307 alloy 0.3%Ag introduced over Two years ago Also worked against Sn/Cu/Ni alloy with large TV Co and they went with 0.3%Ag due to reliabili
Electronics Forum | Tue May 16 17:42:52 EDT 2006 | jbrower
Howdy aj, wow! Be prepared for serious problems with corrosion of your stainless steel workings of your pump. Last I looked changing a wave solder pot over to nitrated coating for electrovert was in the neighborhood of 18-20K. I'm not a betting man
Electronics Forum | Wed Mar 21 11:42:54 EDT 2012 | davef
Downhole solder suggestions, in order of preference are: * Kester Sn96.3Ag3.7. Most vendors do not stock straight tin-silver alloys, whose wallet is that fat? * SAC305 can usually be used in place of one of the copper-free tin-silver alloys in downho
Electronics Forum | Sun Jan 14 12:42:35 EST 2007 | SMTRework
I think the main cause of this condition is #3 because both #1 and #2 never change from board to board, these are identical boards with identical BGA revisions. These BGA's (as stated before) are about 3 years old.. I don't believe they are lead free
Electronics Forum | Mon Apr 26 11:42:29 EDT 1999 | Chrys Shea
| | Hi, | | Im doing some experiments and studies on lead free solders ( any alloys).I would like to get some information on a few lead free solder paste manufacturers and if possible their web page adress and contacts. | | Thanx in anticipation |