Electronics Forum | Sat Jul 04 05:40:23 EDT 2015 | seshadri
Dear Distingushed Friends, I would like to gain some knowledge on X Ray. It is very Confusing for me to understand the difference between the DAGE Transmissive tube Vs YXLON micro focus tube. The Target power Vs Tube power and detailed detectabilit
Electronics Forum | Tue Aug 11 03:27:10 EDT 2015 | iamera
Hello, I am new in this forum and also new in PCB manufacturing. now we have issued about silver open and short. we can detect this defect after auto check process and its to late to save our PCB. Is there any way to detect silver open or insufficien
Electronics Forum | Wed Jan 17 12:10:47 EST 2018 | guilherme_castro
I have the follwing problem in our proccess we have to many problem with via hole and trought plated holes like voids air bubbles . During the eletricial test process our machine is not detecting this problems , the voids and air bubbles How
Electronics Forum | Fri Dec 22 16:28:07 EST 2023 | jeana
I've tried yesterday, I've spray painted a XF nozzle with mat black paint. (with some protection on the tip obviously). It is not really succesful though, Vision still have false detection. When a part is indeed on the tip, it detects it but with
Electronics Forum | Sun Dec 06 14:22:24 EST 2009 | Dany
We use Photondynamics SV-7550 now. We want to upgrade our AOI because we found that SV-7550 are not very good to detect solder defects. I send samples boards at each company with the solder defects that i can't detect with my Photondynamics SV-7550.
Electronics Forum | Mon May 07 09:47:45 EDT 2001 | orbotech
An ultimate truth in AOI is that "you can not avoid what you can not see". At the post solder stage, 2D inspection is typically not enough as it simply "can not see" everything using a single perspective, and therefore, can not detect all of the faul
Electronics Forum | Wed Jan 13 12:17:47 EST 2016 | trampacorp
Thanks for your input Michael. Basically the > boards had been go through from washing and even > ionic contamination already. In order to > eliminate or detect the flux residues, is there > any equipment something like a uv lamp that can > dete
Electronics Forum | Wed May 09 03:29:16 EDT 2001 | Eyal Duzy
Yes, your observation is accurate. Different process steps have different inspection requirements which necessitates employing different imaging technology to ensure the best performance (detection and throughput). Orbotech, for example, offers both
Electronics Forum | Wed Apr 30 08:00:33 EDT 2003 | pjc
Jason, In Transmission AXI the entire solder joint volume is imaged, not just a slice (no missing information) as with Cross-Section. Also, there is no signal loss from mechanical or digital image reconstruction (highest contrast and edge strength).
Electronics Forum | Sat Feb 14 15:47:07 EST 2004 | Larry
Depends a lot on what you want to solve. Very low volume conformation of componpents down to legends, process control or inspection of assembly. Biggest problem is they are resource hogs. Most require constant attention. Any change in component sup