Electronics Forum | Thu Jun 25 08:30:38 EDT 1998 | Earl Moon
| I have a single-sided board with test vias that pass through the board. The test vias are pasted and reflowed with the SMT components on the top side. When the boards are wavesoldered, the solder coverage on the vias is spotty. Some will sold
Electronics Forum | Thu Jun 25 09:29:01 EDT 1998 | Henry Lee
| | I have a single-sided board with test vias that pass through the board. The test vias are pasted and reflowed with the SMT components on the top side. When the boards are wavesoldered, the solder coverage on the vias is spotty. Some will so
Electronics Forum | Wed Jun 24 14:08:34 EDT 1998 | Henry Lee
I have a single-sided board with test vias that pass through the board. The test vias are pasted and reflowed with the SMT components on the top side. When the boards are wavesoldered, the solder coverage on the vias is spotty. Some will solder
Electronics Forum | Thu Jun 25 08:30:39 EDT 1998 | Earl Moon
| I have a single-sided board with test vias that pass through the board. The test vias are pasted and reflowed with the SMT components on the top side. When the boards are wavesoldered, the solder coverage on the vias is spotty. Some will sold
Electronics Forum | Thu Jun 25 09:29:01 EDT 1998 | Henry Lee
| | I have a single-sided board with test vias that pass through the board. The test vias are pasted and reflowed with the SMT components on the top side. When the boards are wavesoldered, the solder coverage on the vias is spotty. Some will so
Electronics Forum | Wed Oct 10 20:35:17 EDT 2001 | djarvis
Stephen, I don't understand this at all mate. 1. If you don't place a QFP and get bridging across the bare pads, you were gonna get absolutely horrendous bridging if you did put one down. That points to poor printer set up or stencil design or both
Electronics Forum | Tue May 31 11:56:12 EDT 2005 | chunks
Hi Matt, Get definitive answers! Contamination on the HASL finish?: From the pix you posted, it looks like something fishy is going on. I�d reject them back to the board house and demand an answer. Most board houses and purchasing people will g
Electronics Forum | Tue Feb 07 13:39:42 EST 2006 | gregoryyork
You can use straight forward Tin/Copper but it flows very poorly so solderability is an issue. Dosing with Phos improves this but need to stay on top of it. We have supplied some 3.8%Ag alloys for flow they work well but you get a small 'chill point'
Electronics Forum | Sun May 21 23:29:38 EDT 2017 | zsoden
Hi all, We run an old Seho 1135C wave solder with a 63/37 pot at 250°C. It has been running well for a couple of years but we have noticed lately that all of the larger pads (terminal blocks, transformers, etc.) require additional solder to be appli
Electronics Forum | Fri Jun 18 10:46:10 EDT 1999 | Scott Cook
| | | first of all what is the technical term for the small amount of solder on a plated pad. we are getting poor screen printing gasketing on a 20 mil qfp due to this solder not being even or too high in spots and not covering the length of the pads