Electronics Forum | Fri Jun 26 14:27:51 EDT 2020 | victorzubashev
Hi Indhu, It could be multiple reasons but probably one root cause. metal nut might require reflow profile change- you need to check it with SMT reflow profiler. the part might be oxidized - you can check solderability or try to solder part using a
Electronics Forum | Sat Oct 01 01:25:30 EDT 2005 | ck
Sorry theres a mistake on previous question. It should be lead free component termination but non lead free solder alloy Sn63/Pb37. The reflow profile i am using : Soaking temp. 120 to 160 deg C; time 90 to 120 sec. Peak temp. 215 to 225 deg C; time
Electronics Forum | Fri Feb 17 09:02:21 EST 2006 | russ
proper pad geometries, accurate placement, and good reflow profile. Are you having problems right now?
Electronics Forum | Mon Feb 18 15:44:49 EST 2008 | ck_the_flip
Yup! All the major players out there - KIC, Datapaq, and ECD - are all capable of profiling both reflow and wave solder. check them out. www.kicthermal.com www.ecd.com www.datapaq.com
Electronics Forum | Thu Aug 12 00:02:29 EDT 1999 | dean
| We currently have 32 LEDs per board and are looking to change the LED from a gull wing package to another package. (possibly a chip type package). I have heard that some cases and LEDs do not like reflow. This part is not cost effective to have to
Electronics Forum | Thu Sep 02 21:02:55 EDT 1999 | Paul Wareham
We've noticed that there are many different recommendations for pad sizes for various SMT parts. This seems to vary wildly from manufacturer to manufacturer for the same case sizes. Is there any standards that can used used to specify these sizes?
Electronics Forum | Thu Apr 18 23:56:27 EDT 2002 | Abelardo Rodriguez
I'm trying to get a better understanding of the cooking process of pcb's. The use of nitrogen in reflow and wave ovens. Seems to have a wide margin of acceptance as a standard gas to prevent oxidation of metals in the board. Has any one heard or us
Electronics Forum | Sat Apr 20 10:12:16 EDT 2002 | davef
If people use an inert gas, they use nitrogen for mass soldering. Inert gases get progressively more expensive as you move down the periodic table. Many times no-clean flux is less active than other flux types. So, people use an inert gas to lower
Electronics Forum | Mon Dec 04 15:37:51 EST 2000 | blnorman
Out of curiosity, what flavor lead-free paste were you using? That's also going to affect the profile.
Electronics Forum | Mon Feb 18 13:11:41 EST 2008 | tonyamenson
Are there profilers that I can use over my leaded and lead-free wave that can also profile my reflow ovens (leaded and lead-free). I'm not that familiar with either but as I learn I can't help but think that there should be something on the market t