Electronics Forum | Mon Jan 18 21:05:15 EST 1999 | Dave F
| I get white residue on my PCBs after vapor degreasing. No comments on the vapor degreaser. Yes, I still use one of these. I use a vapor degreaser and a 1,1,1 replacement solvent due to the quick clean and quick dry times. Anyway, I only get whi
Electronics Forum | Wed Jan 20 21:25:32 EST 1999 | Tony A
| I get white residue on my PCBs after vapor degreasing. No comments on the vapor degreaser. Yes, I still use one of these. I use a vapor degreaser and a 1,1,1 replacement solvent due to the quick clean and quick dry times. Anyway, I only get whi
Electronics Forum | Wed May 03 20:04:21 EDT 2000 | Dave F
Joe: Hey, just hose everyone down with water when your humidity starts to decrease to below 40%. ;-) Actually, that�s how some humidity controllers work, when added to your heating system. Well basically that�s how they work. I�m not tryin� to
Electronics Forum | Thu Jan 14 22:59:08 EST 1999 | Chris G.
I get white residue on my PCBs after vapor degreasing. No comments on the vapor degreaser. Yes, I still use one of these. I use a vapor degreaser and a 1,1,1 replacement solvent due to the quick clean and quick dry times. Anyway, I only get white
Electronics Forum | Wed Sep 29 07:28:04 EDT 1999 | Wolfgang Busko
3�C/min) or maximum temperature (~240-250�C)." For the correct handling of moisture sensitive devices and prebaking advices see IPC-SM-786A or newer publikations. I encountered the following: A tray of sample BGAs was send to me proper packed and se
Electronics Forum | Thu Jun 20 15:05:41 EDT 2002 | carln
I saw this system at one of the last APEX Shows. I was not impressed because of the many downsides and potential hazards. Strapping an electrical device on your hand and placing the device into a liquid is kind of like blow-drying your hair in a ba
Electronics Forum | Mon Apr 12 22:49:09 EDT 2004 | Ken
I will assume the balls of the device are tin-silver or tin-silver-copper??? There is no reason why you can not run 63-37 solder paste on this device. You will form an intermetallic at the interface structure, however, you will NOT form the 2/3 col
Electronics Forum | Mon Feb 13 10:13:50 EST 2006 | slthomas
I have been through this before. At a med. device company they required every device that performed a measurement to be calibrated. O-scopes, calipers, 6-inch steel rules, etc. And thermocouples. While I can't see what difference it makes to the pr
Electronics Forum | Wed Feb 10 18:17:46 EST 1999 | Earl Moon
| Hi, | | Has anyone found any significant differences on profiling using populated and unpopulated boards? Is it worth sacrificing a board to the profile gods? | | Joe | What's the cost of not doing it. In the same breath, why not wait for a sc
Electronics Forum | Tue Jul 30 12:15:15 EDT 2002 | Rick Lathrop
Hi Dave, The paste applied to the board ends up on the tombstone. The pad has a thin covering of solder most of the time, this is why I think they call it a dewet. Occasionally the pad shows some areas of gold and very rarely are some pads not wet at