Electronics Forum | Tue Jun 05 02:10:01 EDT 2018 | buckcho
Hello sir, Limits in SPI can vary a lot, also depending on finishing of the pcb. For example 170% volume on an IC (assuming is fine pitch) can be okay for ENIG, but very bad if HASL. For are I would recommend that you use either 50-130, or 60-135 max
Electronics Forum | Mon Oct 22 08:27:49 EDT 2018 | filipblad
Hi, We're having issues with our mydata tp9 pick'n place. It doesn't go all the way down on the tool, so it can't pick it up or install it. The fault code I get when trying to install tools is F-TLMN-18: Can't reach tool bank. Any ideas? I've comp
Electronics Forum | Thu Mar 28 13:19:14 EDT 2019 | davef
There is no industry standard for BTC stand-off height. "IPC-7093A Design and Assembly Process Implementation for Bottom Termination SMT (BTC) Components" just finished "Final Draft for Industry Review" in December 2018. It mentions stand-off height
Electronics Forum | Tue May 21 13:17:47 EDT 2019 | SMTA-Thomas
2.54 μm [100 μin] gold thickness and all through-hole leads that will be hand soldered regardless of gold thickness” (we automatically solder wash all components which violate this requirement). In all cases we have attempted different no clean flux
Electronics Forum | Thu Apr 09 11:49:49 EDT 2020 | stephendo
I don't think that there is an industry standard on that. Each machine manufacturer will have to say what they mean. I think the first option looks at what you taught and then looks at what it sees when looking for the fiducial. The other method sou
Electronics Forum | Mon Jun 15 16:31:25 EDT 2020 | rgduval
You may find some wetting issues running LF HASL with 63/37, as your reflow temperatures will be significantly below the LF reflow. On fiducials...if you don't have a quote for your boards with ENIG, I would recommend at least checking it out. It's
Electronics Forum | Thu Sep 17 18:22:06 EDT 2020 | astarotf
Hello We have a GSM machine with two heads from the universal company, currently the machine fails to zero and in production mode, when the heads increase the displacement speed in the Y axis, they stop immediately. And the error illustrated in the i
Electronics Forum | Thu May 13 20:40:25 EDT 2021 | winston_one
Yes, we can't use pure Pb PROCESS. And as I say we will not use it anyway, as we have lead-free BGA's, LGAs, component with Solder Charged Terminations... It's became almost normal practice to solder it with leaded solder pastes. In this case peak re
Electronics Forum | Fri May 14 07:00:32 EDT 2021 | tommy_magyar
Hi Daisy, I have worked with Viscom AOI before, I am in training with Omron now, but there were many times when this happened to me in the past. Recommended things to do: - Check for duplicated analysis - the AOI might spend time with taking pictur
Electronics Forum | Tue Jul 05 17:09:40 EDT 2022 | madisreivik
PROBLEM SOLVED :) ! I messed with parameters, then started to check hardware again. and.... There are 2 transport position on the carrier 1) vacuum 2) mech clamp Both have fiber position sensor which shows the status When there is component, the