| Hello Netters, | | I have a customer who wants us to aquaeos wash a PCB after all operations have been performed. The PWB is two layer FR4 with a Transformer, a Multichip Module with Conformal Coating, (6) 11" insulated wires that are tinned on e
Electronics Forum | Fri Aug 12 22:10:24 EDT 2005 | Mika
I agree with all the prior postings! But I have some additional thoughts about this. If there is a build up of moistures (% humidity) inside the pcb; before you reflow the pcba; then you will have the result out of the oven, just as you described. My
Electronics Forum | Wed Dec 17 10:25:47 EST 2003 | blnorman
I may have asked this question before but couldn't find anything when I ran a search. Question, after ultrasonically cleaning our boards we bake them out to drive off residual moisture. Current requirement is 24 hours @ 105�C. I seem to remember a
Electronics Forum | Wed Dec 17 14:38:25 EST 2003 | davef
Francois Monette [Cogiscan Inc. 450-534-2644 fmonette@cogiscan.com ] is the resident genius on component and board baking. If he doesn't chime-in a in a day or so, give him a shout. He seems to nap quite a bit. Alternately, if you search on his na
Electronics Forum | Sun Jan 19 10:45:04 EST 2003 | davef
For laminated FR4 PCB, we bake between 6 and 24 hours at 100�C. [Search for other bake recipes in the fine SMTnet Archives.] Alot of the determination of baking time is a function of: * Amount of moisture absorbed. * Amount of moisture you need to r
Electronics Forum | Mon Dec 08 18:25:35 EST 2008 | yuepingwu
Hi Bob, Do you have information about IPC D-35 for reference? What moisture sensitive level is the Sn-Pb/RoHS of PWB? Does PWB supplier start to implement PWB drying packaging?
Electronics Forum | Tue Jul 20 15:02:49 EDT 2010 | vetteboy86
I've seen this warp issue across several different PCB's we assemble. One of the biggest head ache's is getting the boards to transfer between machines, converyors, and inside our pick and place. Due to the warpage, transport between conveyors is dif
Electronics Forum | Mon Sep 06 20:18:37 EDT 2004 | charly
hi, we are running high mixed low volume here, and i encounter many pcb delam after reflow issue. here some doubt need ur advise: 1. actually, what is max temperature and duration can a bare PCB reflow without any quality problem? if i allow bare
Electronics Forum | Fri Jun 01 23:57:21 EDT 2012 | bwjm
HI Guys, i am facing similar issues with this BT resin material too. PCB specs are 4 layers, Nelco400013, same Tg and Td. My PCB delam after reflow. The PCB has both side mounted with SMDs. Initial mounting on the btm side after reflow, no delam. B
Electronics Forum | Mon Apr 12 08:10:17 EDT 2004 | wgaffubar
We are sometimes, not always, seeing very large voids in the solder joints of BGA's with Via in Pad. Some lots of PCB will have the voids and other lots of boards will not. I feel the via's are outgassing during reflow, due to the PCB not having been
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830