Electronics Forum | Mon Nov 23 15:26:35 EST 2009 | davef
confo* and bubb*] to fine threads like: http://www.smtnet.com/Forums/Index.cfm?CFApp=1&Message_ID=59681
Electronics Forum | Wed Nov 25 15:16:04 EST 2009 | sforman1
Why in heavens name are you using a heat or air cure conformal coating. Why aren't you using a 100% solids UV cure system. You would never have an issue like this Sam Forman MicroCoat Technologies
Electronics Forum | Mon Nov 30 23:11:50 EST 2009 | prodivegsr
Hi sforman1 Are you refering that the UV is able to cure on solvent based material too ?
Electronics Forum | Wed Dec 02 09:04:48 EST 2009 | sforman1
Josh: This is your choice. It wouldn't be mine. Again, I have been doing this for well over 40 years (http://www.m-coat.com) Sam
Electronics Forum | Wed Feb 16 12:22:54 EST 2011 | duso02
Have you always used xylene? For our 1B73 we use nothing but 73 thinner from Humiseal or PGMEA at about 50/50 depending on the humidity.
Electronics Forum | Fri Mar 04 07:31:51 EST 2011 | duso02
Dennis, I'm amazed that you are having this much trouble. Not trying to be a smart-a**, it's just that 73 is usually pretty easy to fix. Is there anyway you could send me some pics of what you are seeing?
Electronics Forum | Fri Mar 04 10:45:43 EST 2011 | dennisfo
I'll try to get some pictures using the Ersa scope this afternoon. Not sure how to post them,may try to send directly to you.I'll take some immediately after coating then of the same after a flash off period.
Electronics Forum | Wed Jul 06 15:52:36 EDT 2011 | duso02
Ricky What silicone coating are you using? Are you using at as a coating or as a potting? In other words how thick are you applying it.
Electronics Forum | Wed Jul 06 20:05:02 EDT 2011 | rickysanchez
we are using the silicone Dow Corning JCR6101UP. we use it to coat the whole die including the wires.
Electronics Forum | Mon Jul 11 11:40:11 EDT 2011 | blnorman
According to the datasheet, this is a LED encapsulant, is that how you are using it? It also had a section on compatibility, which indicates that it is an addition-cure silicone prone to cure inhibition.
.gif)