Electronics Forum | Thu May 20 07:52:36 EDT 2010 | rgduval
In general, cleaning with deionized water is acceptable for most component. Open switches and contacts, in general, do not get damaged in this process. A good drying is required, of course, after washing. However, you've described dewetting issues
Electronics Forum | Fri Dec 10 12:24:46 EST 2010 | davef
Causes of dewetting in conformal coating. Factors that influence dewetting usually involve non-ionic contamination such as: * Residues from board manufacture including silicone surfactants from solder resist & HASL rinse contamination * Component res
Electronics Forum | Thu Feb 09 20:12:51 EST 2017 | imarkl
Any advise about dewetting defect occurrence during 2nd pass reflow. Commonality on affected PCB having water marks near affected pad(s). Elemental composition found on affected pads without solder paste are Silicon and Sulfur. As well as in pad with
Electronics Forum | Thu Apr 20 03:50:35 EDT 2017 | cromaclear
To overcome the dewetting issues of the past, a number of techniques have been used such as alternating directions on the wetted nozzle; this helps to avoid the solder biasing to one side causing the other side to oxidize and de-wet. Another method o
Electronics Forum | Thu Nov 02 22:11:46 EST 2000 | Dason C
Please check with Fab house, what is the thickness of the immersion gold if the gold thicknesss is less than say 2.5 micron, you will found dewetting or open. It is recommend the gold thickness is around 5 micron. Good Luck Dason
Electronics Forum | Mon Oct 22 09:32:27 EDT 2001 | Steve L
The solder joint appeared dull and there is dewetting on the PCB after Reflow. The leads of IC we used appeared dull grey before soldering. Dose anyone happen to know if there is a standard to verify the IC contamination and how to deal with the con
Electronics Forum | Thu Nov 01 12:13:10 EST 2001 | jonathan
I guess this clarifies the defect more then looks at the process, but I�ll just through it out there for the sake of learning something new. If anyone would comment on this please feel free�. There are many different varieties of dewetting defects.
Electronics Forum | Wed Dec 19 10:21:16 EST 2001 | davef
Crank-up the volume. Look here for a similar discussion http://www.smtnet.com//forums/index.cfm?fuseaction=view_thread&CFApp=1&Thread_ID=4735&#Message18380&
Electronics Forum | Fri Mar 07 15:07:50 EST 2003 | davef
YiEng, MA/NY DDave: Usually when the gold plating bath goes south, you loose solderability.
Electronics Forum | Sun Mar 09 19:55:56 EST 2003 | iman
Which specific title books from under your pen, would you recommend for the avid process reader/learner? specific - talking about info/process/data wealth books, and not which books give the most royalties *grinz*