Electronics Forum | Thu Nov 04 21:36:36 EST 1999 | chris
Hi John, Thanks to your reply, just one question is it possible that the solder paste ( flux material )applied to the pads cause the non-wet. regards Chris
Electronics Forum | Fri Nov 05 10:01:04 EST 1999 | Dave F
Chris: You can have more than "one question!!!" Anyhow, yes crappy solder paste can cause non-wetting, but before you go there understand why the paste is wetting some surfaces, but not others. Ta Dave F
Electronics Forum | Tue Dec 14 07:48:23 EST 2004 | grayman
Can you provide me with non water base chemical ( 1 part only) for cleaning non water soluble flux and earth friendly. I would appreciate very much if you can also give me contact info. Arman
Electronics Forum | Wed Oct 05 10:52:28 EDT 2005 | Rob
Sorry for the miss-understanding - there are at least 2 types of MSD cards - reversible & non reversible. We use the non-reversible type. Once exposed they record the max humidity through a one way chemical reaction.
Electronics Forum | Tue Jan 24 11:59:55 EST 2006 | Chunks
Tell your board house/customers you want "non-smobc". hich stands for non-solder maske over bare copper. MPMs love exposed fids in just about any finish. You can always use pads on an MPM too.
Electronics Forum | Thu Jun 22 15:49:53 EDT 2006 | samir
Shocker, You truly live up to your name with those "sexist" remarks! Are you Islamic? "Mumtaz" is an Indian/Arab name. As for me, my wife converted me to become non-muslim...probably the non-practicing muslim here in Riyadh...
Electronics Forum | Fri Jun 30 08:20:14 EDT 2006 | davef
Distributors and dealers can ship non-ROHS parts forever. Assemblers can not ship non-ROHS products to Euroland after July 1 and other counties [Japan, Korea, China, California, etc] after their cutoff dates.
Electronics Forum | Mon Sep 11 19:17:07 EDT 2006 | russ
if you did not take PCB temp over about 245 C you got no probs buddy. just non compliance most likely. Fiberglass and copper, not much can happen there Russ
Electronics Forum | Thu Feb 01 09:58:15 EST 2007 | blnorman
Distilled water normally removes ions as well as dissolved solids (non-volatiles). Deionized water has been stipped of ionic species, but non-ionic organics are left behind.
Electronics Forum | Mon Apr 02 09:03:35 EDT 2007 | P.Saravanan
What i want to know is If we are using RoHS compliance component in Non RoHS process means leaded process is there any solderability issue ?