Electronics Forum | Wed Feb 18 12:42:43 EST 2004 | babe
OK, if the sphere of the ball and the paste on the pad are both eutectic, 63/37 then the paste will reflow first causing a drop of the component, after which the spheres will reflow causing a double drop and a good intermettalic. You can see this by
Electronics Forum | Fri Feb 20 13:01:26 EST 2004 | Jay
First, it depends on the alloy composition of the solder. As you might know, eutectic Sn/Pb solder has the lowest melting point among available conventional solder systems. (except those based on Sn-In and Sn-Bi systems.) For example, 63Sn/37Pb - 183
Electronics Forum | Wed Sep 02 06:50:55 EDT 1998 | Masdi Muhammad
Hi, We are having problem with yield loss due to electrical fail. Further investigation shows that the failure is due to solder bridging under BGA. Has been there any study or experience on how this could occur and what we can do to prevent it. Than
Electronics Forum | Fri Oct 26 11:09:13 EDT 2007 | hussman
Even a proper solder joint will fail if the rite stresses are applied to it. Sounds like you have an over heating issues, not a solder issue.
Electronics Forum | Fri May 07 17:02:01 EDT 1999 | Earl Moon
| On 1.27mm (0.050 inches) Standard Ball Grid Array's. | The ball size diameter starts at approximately 0.025 inches. | | If the ball size decreases to 0.012 inches (due to the solder flowing down a via) is the solder connection reliable? | | This
Electronics Forum | Thu May 13 18:36:55 EDT 1999 | Andrew Wulff
| | On 1.27mm (0.050 inches) Standard Ball Grid Array's. | | The ball size diameter starts at approximately 0.025 inches. | | | | If the ball size decreases to 0.012 inches (due to the solder flowing down a via) is the solder connection reliable? |
Electronics Forum | Fri Feb 13 11:19:07 EST 2004 | Evtimov
Hi Bryan The answer is in the paste compozition. Balls of the BGA are usually made by eutetic solder paste.
Electronics Forum | Thu Feb 12 10:19:46 EST 2004 | Bryan
Hi all, These days our customer asks us to figure out ,during reflow,the BGA ball and solder paste,which will first melt? I think it's very hard to get the rusult.coz I think it'll vary at diffrent part of the BGA,and how can this affect the perf
Electronics Forum | Fri Feb 13 11:46:23 EST 2004 | Jack
Is your customer trying to reduce voiding? If the device is using Sn90 / Pb10 and the paste is Sn63/Pb37 the board will melt first. However, if both solders are 183C eutectic, it's a tossup? PCB design, copper weight, bga type (pbga, micro bga, Tbg
Electronics Forum | Fri Feb 27 11:33:32 EST 2004 | Bryan
Very strange question,but interesting.Is there anyone who have conducted any experiments to figure out the results?I made a profile board,one thermal couple on pad and other one drilled into the ball of BGA.the 2 points are perpendicular to conveyor