Electronics Forum | Wed Jul 28 07:59:50 EDT 2004 | cyber_wolf
Ken, With all due respect: Surface mount is surface mount. Whether you are placing 0201's, or PLCC84's the basic concept is the same. So I would surely hope that for the most part my process is transferable. I guess I was too broad when I said "we n
Electronics Forum | Thu Oct 26 11:49:54 EDT 2006 | sms_don
CW, The good news is that you are not trying to use SAC paste with SnPb balls for that would be a void generator due to the ball being liquidous while the SAC paste is still in a flux cleaning stage. Two points to consider: One, voids are not an i
Electronics Forum | Mon Feb 06 22:38:46 EST 2017 | david_chiu
No matter in selective soldering or wave soldering process, higher pot temperature and longer wetting time can increase IMC thickness and joint strength(reliability), but as Daivf said, you need to care if the DIP component and bare PCB was damaged b
Electronics Forum | Wed Sep 12 12:55:34 EDT 2001 | stevearneson
The CyberOptics LSM 300 cannot provide true 3D volumetric measurements. It is impossible to measure volume using a "Box" that is drawn around a feature without the same characteristics. Owners of the LSM 300 try it for yourself. Move the stripe ar
Electronics Forum | Wed Jun 02 05:40:35 EDT 2004 | johnwnz
Is there not an issue with reflowign the SAC ball's in term's of drivign up the lead contect in a lead free joint that increases the risk of failure in them? certainly dramatically increases voiding... have some pictures of soem that a customer tried
Electronics Forum | Fri Feb 23 10:10:32 EST 2024 | emanuel
Well, the story is a little more complicated. The product is also an LED lamp made on an aluminum PCB with the LEDs on one side and the drivers on the other. The board itself is not big, about 90x90mm and most of the components are soldering well. Us
Electronics Forum | Mon May 07 16:07:05 EDT 2012 | davef
Start with targets based on the stencil thickness (for height) and stencil thickness times the aperture size (for volume). * Set reasonable upper and lower control limits (+ 25% and –25 % of the targets, for example). * Next, check the printer set-u
Electronics Forum | Tue Jul 19 09:18:14 EDT 2011 | davef
Could this be an opportunity to explore the use of cartridge-type paste dispensers? Or maybe a reason to keep working over the weekend. * Re-Storing & Re-Using “Used” Solder Paste. Though not a recommended practice, used solder paste from the stenci
Electronics Forum | Tue Apr 13 08:21:05 EDT 2010 | esca
Hi manchella, After ATC test, two different failure modes can be present: solder FATIGUE (into bulk) or BRITTLE INTERMETALLIC fracture. So, first you have to verify this. Moreover, which brand of SMT paste have you used ? The crack into solder joint
Electronics Forum | Tue Jun 22 08:52:09 EDT 1999 | Cunli Jia
| | | I swear I posted it! I smoked an entire cigarette waiting for the damn thing to upload! I'll try it again when I get home tonight. | | | | | | Sorry for the inconvenience. | | | | | | | | | | | regular or filter? | | I am having the same