Electronics Forum | Wed Aug 11 15:58:39 EDT 1999 | Doug Philbrick
| We are using a mixed technology process with mostly through-hole parts plus some SMT IC's on the component side and some passive SMT parts on the solder side. We do not have a proper wave soldering machine for doing solder side SMT (double wave or
Electronics Forum | Thu Aug 12 19:30:22 EDT 1999 | Kris Harris
| We are using a mixed technology process with mostly through-hole parts plus some SMT IC's on the component side and some passive SMT parts on the solder side. We do not have a proper wave soldering machine for doing solder side SMT (double wave or
Electronics Forum | Thu Dec 08 22:24:48 EST 2016 | anhsang38
We are currently using wave solder pallet for our wave soldring process. I want to find a solder pallet cleaner machine that for cleaning pallet. Does anyone know where can i buy this machine. Pls, advise me for this case.
Electronics Forum | Tue May 23 02:32:33 EDT 2017 | bukas
hello Zac, if you are running pump at 100% and there is not enough wave then you will probably need to empty solder bath and clean everything. also check pump parts for tear and wear. eached solder inlet can make a lot of problems when it comes to w
Electronics Forum | Wed Feb 06 02:14:43 EST 2008 | mun4o
Hi, we use Vitronics Delta 6622 solder wave.I try to adjust high of backplate, but I don't know whether the adjustment is correctly.Now, when the frame enter in the main wave, solder flow in the same direction as PCB.But when the frame go above main
Electronics Forum | Fri Jan 28 12:30:57 EST 2005 | glenda
We are looking for a used or new wave machine must be able to do lead free solder. Does anyone have contact information in the Chicago, il area for used wave soldering machines? Thanks for any help we can get.
Electronics Forum | Fri Sep 09 15:50:08 EDT 2005 | chunks
The hand assembled part is soldered in? If so, the white residue may be from the operator using some added wave solder flux to get better wetting when hand soldering.
Electronics Forum | Mon Nov 23 20:16:11 EST 2009 | davef
We're not familiar with Loctite 3606. Adhesive bond strength must be adequate to survive handling forces between the adhesive cure station and the soldering station. At the soldering station, the adhesive will soften during the preheat stage and in
Electronics Forum | Thu Nov 08 10:05:04 EST 2007 | pjc
I have not seen hold size as an issue when switching Sn/Pb to Pb Free wave soldering. Trying increasing your dwell time in the wave- typical for Sn/Pb is 2 to 3 seconds. Try 5 seconds to see what you get.
Electronics Forum | Wed Dec 10 03:15:43 EST 2008 | meritajs
We have had expierience to convert our wave solder machine EPK1(1995g)with cast iron solder pot for lead free SN100.It runs about year and half now without problem.