Electronics Forum | Thu Nov 01 04:32:52 EST 2001 | wbu
Jonathan, we do that all day. We do not use different pastes nor do we glue components nor do we run different profiles. Depends on what is meant by "small components". In our case it�s all that "bird seed" up to SO8. That will work for more parts.
Electronics Forum | Tue Nov 27 13:36:22 EST 2001 | jmathis
Solder balls on the topside of our wave solder boards is a real issue. We have found that during the wave solder process, solder will enter through the via holes in the form of solder balls. It seems to be related to flux captured in the vias and o
Electronics Forum | Fri Dec 07 08:32:56 EST 2001 | scottdavies
I have used Multicore MP-100 and Heraeus F380 pastes for a while, and experienced very few dry joint problems. May be worth checking if the pad size and/or spacing are to the correct specification for the components. Check the date codes on the comp
Electronics Forum | Mon Jan 28 07:40:40 EST 2002 | cnotebaert
Yes and Yes, Your solder supplier should recomend a profile (standard profile) in most cases you can follow it. Of course you should be running a thermal profile of each board type to verify it is within the specified temp rang. You should also chec
Electronics Forum | Mon Feb 18 09:49:04 EST 2002 | Ashok Dhawan
Anyone using Kester 959 flux on Spray fluxer ? I noticed a black coating on filter element which is installed in supply line ( inside flux tank). The filter element is immersed into flux tank. It is turning blackish due to deposit of flux rosin ?? T
Electronics Forum | Mon Apr 15 21:27:16 EDT 2002 | djarvis
Everything we do is RF and have had no problems in the last 7 years with - Indium NC-SMQ92J, Sn63 Pb 37, 90.25% Metal, -325+500 mesh. Stencils are always 0.005" thick. However I will qualify that by adding we are an OEM and each new product may requi
Electronics Forum | Tue May 07 07:41:33 EDT 2002 | Sir Alexandr
Hello ! That was an one of our troubles. But we decidet it. Our way : 1. Vibrofeeders of Phillips may be ajusted for special ironrails , horisontallylairs , so IC goes permanently and correctly, also we create some acceptable subfeeder for Phillips
Electronics Forum | Thu Apr 25 21:58:54 EDT 2002 | Gang shen
thank all of your kind help.today I set the camera gain and offset same as the camera2,the gain is 180,and the offset is 105. First the vision process is failed to pass ,later I found the size of the BGA ball in the screen is so smaller than the rea
Electronics Forum | Thu May 02 10:27:18 EDT 2002 | BTaylor
I have used Quad/ Now Tyco since the early 90s starting with the 4c then on to the QSA-30s, APS-1, and now the Meridian 1010. We have six machines in a very small area and place over 10 million components per month. As others have said the service is
Electronics Forum | Thu May 09 11:59:34 EDT 2002 | russ
One thing I have done in the past although it may not be feasable in your case, is to process through normal reflow and then saturate parts with a high solids water soluble flux and re-reflow with hot air, iron, or even another pass through the oven.