Electronics Forum | Thu Nov 13 06:00:24 EST 2003 | stefwitt
The Siplace web-site will not help you very much, because the HS 180 does not belong to the Siplace line. All the older Siemens machines operate with HP Basic and the computer hardware can't even be replaced with DOS based PC's. Dependent what type
Electronics Forum | Fri Dec 05 08:30:55 EST 2003 | pjc
If your operation is hi-mix low-volume, consider taking a look at some of the bench-top units out there. They are lower cost but can give similar performance as higher cost in-line systems. Some of the bench-tops cannot do solder fillet inspections t
Electronics Forum | Wed Dec 10 15:45:02 EST 2003 | Carl
If your operation is hi-mix low-volume, consider > taking a look at some of the bench-top units out > there. They are lower cost but can give similar > performance as higher cost in-line systems. Some > of the bench-tops cannot do solder fillet
Electronics Forum | Tue Dec 16 06:42:51 EST 2003 | Kev
I am having problems achieving correct pre-heater temperatures with our Hollis solder wave. Our original "Verification Golden board" program uses a conveyor speed of 5ft per minute and pre-heat temps of 300, 350, 400 respectively. Our "golden Board"
Electronics Forum | Tue Jan 13 16:01:06 EST 2004 | russ
I believe that solder paste will need to be applied to this part. I have re-balled these in the past in a low volume situation and here is what I did and there appears to be no adverse effects to the component. Get a stencil (I use 8 mil for .032"
Electronics Forum | Thu Feb 12 13:01:12 EST 2004 | patthemack
Thanks for your response. This is a DeHaart MPC-29. It has manual vision, no conveyor. When I bought it, only one camera was working. I fixed that, but while I was jacking with that, the electronic pressure regulator (spcjr) burned up without warning
Electronics Forum | Wed Mar 31 21:08:34 EST 2004 | Ed
Hey guys. I've been manually dunking circuit boards for 8 years now. I too have the excess residue issue to contend with. I'm using a low solids - no clean flux from Kester (959). I have used solvents, thinners, windex and a multititude of cleane
Electronics Forum | Fri Apr 16 11:03:35 EDT 2004 | davef
Your copper corrosion is not good. It indicates that you have not done a good job in cleaning. [We assume this is a medium green color, not unlike the color of the solder mask on your board, that is almost like a translucent lacquer; rather than th
Electronics Forum | Thu Apr 29 15:21:07 EDT 2004 | davef
Suppliers of laser soldering equipment will probably give you their customer list [just recognize that the engineers that bought the equipment could present interesting points of reference]. Try: * Contax Ltd Little Park Farm Road Segensworth West
Electronics Forum | Wed May 12 01:40:56 EDT 2004 | Grant Petty
Hi, Thanks for all the advice, and we are looking at everything we know of, but have not had much info back from anyone at Universal yet. We have been interested in their machines too and are going to go to a trade show before we decide. However I