Electronics Forum | Sun Sep 04 01:59:41 EDT 2005 | smartasp
We need to dry and clean the air in our dedicated poting and conformal coating room. Can anybody help on how to go about it. The airconditions only recycle and dry until room temperature is reached and therefore have great fluctuations and unstable p
Electronics Forum | Tue Sep 27 08:22:27 EDT 2005 | Amol
I am using masking tape, the 3M high temp blue masking tape. the problem though doesnt seem to be related to the masking tap as i am seeing pin holes and eventual dewets over entire ckt board (its almost as if the board has chickenpox under black lig
Electronics Forum | Thu Aug 24 16:08:18 EDT 2006 | Frank R.
Thanks Bill and Dave for your help, Sorry Dave if I didn't search for information in archives. After wave process we have 2 ICT, 2 AOI machines 4 PVA conformal coating machine that will be use on 3 different lines. The quind of automation I want to
Electronics Forum | Mon Feb 05 10:21:21 EST 2007 | davef
Thermal conductivity [W/m-�C] * Silver: 418 * Aluminum: 403 * Copper [rolled annealed]: 392 * Copper [electrodeposited]: 392 * Gold: 297 * Nickel: 90.7 * Tin: 73 * SAC: 73 * Castin: 57 * Pb37Sn63: 51 * Lead: 35 * Epoxy, phenolic: 25-75 * Conformal co
Electronics Forum | Mon Mar 05 22:51:05 EST 2007 | davef
Humiseal * HT500 HumiTape silicone free (Kapton tape isn't) * HT600 HumiTape [ESD safe version] Try: Shercon [10425 Slusher Dr, Santa Fe Springs, CA 90670; 800-228-3218 F800-955-8988 562-946-8555 F562-946-1015 http://www.shercon.com] "Conformal Coa
Electronics Forum | Mon Mar 05 15:29:50 EST 2007 | ck_the_flip
When no-clean flux and no-clean soldering first came out in the late 80's / early 90's, there were lots of White Papers written about conformal coating adhesion and no-clean flux. I'm pretty sure all CC's will adhere to today's chemistries. To be o
Electronics Forum | Mon Jun 25 11:55:47 EDT 2007 | ck_the_flip
I don't think THEY (Humiseal) know how their material cures. I have a data sheet from them for 1B73, and it says 24 hours at room temperature or 30 min. @ 170�F. We use our in-line oven mainly to dry the material and make it tack-free. You would
Electronics Forum | Thu Mar 27 16:40:45 EDT 2008 | slthomas
(or just some static-safe foam tape) I need to seal a wire terminal block to a board for conformal coating purposes. Currently we glue it to a shim and glue the shim to the board (yuck), but I want to use die cut gaskets if I can make it cost effec
Electronics Forum | Wed Jun 11 10:23:07 EDT 2008 | charliedci
Hi, > > we have to print a serial barcode on a low > volume PCB. For another module we just used our > laser printer and cut the labels to > size. > > However, those laser labels are easy to > rub off, and the new labels are much > smaller. >
Electronics Forum | Fri Oct 23 15:43:31 EDT 2009 | seankim10
According to 5.2.6.1, it states that defected if Solder balls are not entrapped in no-clean residue or conformal coating. How do you define entrapment or how do you assess if the balls won't dislodge under normal product service environment? The sold
Lewis and Clark is your #1 Pre-Owned Surface Mount and In-Circuit Test equipment supplier. We offer a variety of equipment solutions at a significant cost savings over new.
Manufacturer / Equipment Dealer / Broker / Auctions
18 Celina Ave., Unit 16
Nashua, NH USA
Phone: (603) 594-4229