Electronics Forum | Wed Mar 04 10:36:10 EST 2009 | milroy
Hi If you mean your PCB stayed in the Reflow oven more than the reflow time required for the solder paste specs then I suggest to throw away the board because it would lead over heated solder joints all over the board. Think what could happen to an
Electronics Forum | Thu Mar 05 09:46:12 EST 2009 | davef
Solder mask requirements: * IPC-6012 and IPC-SM-840 contain detailed specifications and information regarding solder mask requirements. * IPC-A-600 defines acceptability of printed boards [analog of A-610 for board assemblies]. Why can't you use A-6
Electronics Forum | Fri Mar 20 10:27:58 EDT 2009 | joelperez
Hello, Has anyone dealt with the process of listing the substances on their electronic products due to REACH? I'm trying to find out if there is a way to globally calculate the area ratio of all the apertures on a solder paste stencil so I can calcu
Electronics Forum | Fri May 01 07:22:56 EDT 2009 | kareal
In my project of flip chip PGA production , I found serious delamination in interface of solder mask and first layer copper trace of substrate after UHAST 96hrs( 130C, 85%RH) reliability test. The delamination are always around one type solder bump,
Electronics Forum | Mon May 11 02:19:06 EDT 2009 | malmsteen
Hi PCB experts, I am tasked to design boards (medical) that can stand -90 Deg C environment. I am seeking for help from all the PCb experts out there in guiding me on the right selection of PCB materials, soldering alloy (SMT & Wave) and right comp
Electronics Forum | Fri May 15 08:04:32 EDT 2009 | rwyman
higher temp/shorter time). Solder mask may be a factor as well. I've seen parts get knocked off where the glue is still affixed to the part, along with a nice piece of solder mask from the board. If you can knock a part off with casual contact, th
Electronics Forum | Tue May 26 10:23:53 EDT 2009 | mun4o
hi, i am proccess eng solder wave process.I have problem with a PCB.There have ceramic SMD capacitor, SMD thermistor and SMD inductor 1uH.After reflow all is OK, but after SW these components are broken???The pin is separated from the body???the que
Electronics Forum | Mon Jun 29 10:19:25 EDT 2009 | brandieatborisch
Are there any photos available of what good HASL finish looks like as opposed to not desired? I'm looking for something to use as an aide in inspection becasue sometimes boards at our facility are received with HASL where the solder is excessive cau
Electronics Forum | Tue Jul 28 13:27:31 EDT 2009 | davef
It's possible that there is limited application of "3M™ XYZ-Axis Electrically Conductive Adhesive Transfer Tape 9719" similar to your intended use. What do 3M™ application types say? Certainly high temperature soldering would make a mess of a piezoc
Electronics Forum | Fri Aug 07 15:56:56 EDT 2009 | davef
Well, since you've gotten no takers, we'll launch in to this with careful analysis and introspection, fully aware that we're likely to get 'blasted' for any number of reasons. The most critical parameters to monitor for proper wave solder machine pr