Electronics Forum | Wed Jun 03 14:37:53 EDT 1998 | Anthony
I really appreciate everybody taking the time to help me out with this problem. I'm going to run your input by the design engineer, after that I may be taking you up on that offer to contact you Earl. Again; thank you! Anthony | If your board is si
Electronics Forum | Wed Mar 28 18:23:48 EST 2001 | Mike Konrad
Hi Bill, Please let me refresh your memory� On April 1, 1999, the United States Environmental Protection Agency sent you a letter based on what they called �inaccurate� statements made by SmartSonic (ironically on SMTNET.COM). EPA letter dated Apr
Electronics Forum | Thu Oct 26 12:56:50 EDT 2000 | ptvianc
That is a tough question. I think that an important point must be made, and that is that the electronics assembly business is just that, a business. And, electronics asssembly companies are in business to make a profit. The profit, or "bottom line
Electronics Forum | Tue Nov 02 17:52:17 EST 1999 | Dave F
Jim: Several points: 1 If you�re correct about corrosion of your component leads (which is entirely possible if the leads are steel, as you say), then the AIM 264-5 no-clean may not be aggressive enough to remove the corrosion you are seeing routin
Electronics Forum | Wed Jun 09 17:29:59 EDT 1999 | Earl Moon
| I am starting a new project which involve 3 oz copper layer with 20 mil components on the top of the board and 0.040" thick copper with D2Pak on the bottom of the board. | There is anybody has experience on metal-based PCB reflow process? I guess
Electronics Forum | Thu Jun 10 11:23:10 EDT 1999 | Gang Pan
| | I am starting a new project which involve 3 oz copper layer with 20 mil components on the top of the board and 0.040" thick copper with D2Pak on the bottom of the board. | | There is anybody has experience on metal-based PCB reflow process? I g
Electronics Forum | Fri Jun 05 13:06:14 EDT 1998 | Steve Schrader
| If you could measure and chart 3 variables in my process, what would they be? | The boards that I produce are on panels that are 12up and 2x4 up. All boards are single sided paper base w/o plated thru holes. They are on scored panels that measure
Electronics Forum | Thu Jun 04 15:41:07 EDT 1998 | Chrys
| If you could measure and chart 3 variables in my process, what would they be? | The boards that I produce are on panels that are 12up and 2x4 up. All boards are single sided paper base w/o plated thru holes. They are on scored panels that measure
Electronics Forum | Thu May 07 12:54:01 EDT 1998 | DARRYL SCHLOSSER
| I am running a board that is .062" thick and has components that over hang the edge of the board by .090". I have bottom side smt components (chip caps and resistors only) and use the turbulent wave to help solder the components. The problem I am
Electronics Forum | Thu Oct 17 11:36:09 EDT 2002 | bdoyle
I think I follow the questions... Ok lets see. About two site revisions ago there was a "home" page and there was a "MySMTnet" page. They were completely seperate entities. MySMTnet is a registered user customizable page. You dictate what boxes