Electronics Forum | Tue Dec 03 18:51:57 EST 2019 | kylehunter
Hi all, We are having a confusing defect with one of our client's boards. It is a large board, 30" x 12". The client supplies the LEDs, they are cheap overseas diodes, and it is not uncommon to have reels with the packaging torn. We have w
Electronics Forum | Wed Dec 04 10:59:04 EST 2019 | dwl
The solder looks a little grainy for Sn/Pb solder but that might just be the picture quality. There appears to be plenty of solder on the pads, so I'd rule out anything to do with the stencil. One possibility that springs to mind; how long is your
Electronics Forum | Thu May 06 19:13:24 EDT 2004 | Greg York
Watch your dwell time especially if larger components. Problem is normally associated with lower temp as well as insufficient flux coverage with larger massed boards or ground planes. Try to hand spray a board to check that fluxer operation is OK. If
Electronics Forum | Fri Dec 30 11:31:32 EST 2016 | horchak
First profilers are expensive and you can use temperature dots for setting up a wave. You stick them to the top side of the board and they change color based on temp. Top side temp should be around 250f or 125c when it hits the fountain. If you spra
Electronics Forum | Mon Sep 03 09:48:12 EDT 2007 | davef
Joris We don�t know the maximum period to store the boards without having problems with blowholes. Too many variables to determine. We prefer to just fix the problem, but understand that you have stock that you need to build-down. Determining mois
Electronics Forum | Thu Mar 25 14:00:45 EST 1999 | Bob Willis
| Rob, | | We are also using intrusive reflow to simultaneously process SMT and Thru-hole components. Our arrangement goes as follows: | | - Screen print solder paste to the single sided PCB using 0.008" laser cut stencil. | - Apply adhesive dots
Electronics Forum | Tue Mar 23 04:07:44 EST 1999 | Scott Davies
Rob, We are also using intrusive reflow to simultaneously process SMT and Thru-hole components. Our arrangement goes as follows: - Screen print solder paste to the single sided PCB using 0.008" laser cut stencil. - Apply adhesive dots to selected
Electronics Forum | Mon Oct 29 19:48:03 EST 2001 | davef
Sounds like the connector is not solderable. * Do they take solder when hand soldering? * Do they take solder when using a hotter flux than you normally use? * What flux are you using? * What are the materials used in fabricating these connector le
Electronics Forum | Thu Jul 29 11:34:27 EDT 1999 | Justin Medernach
| | | | | | Presently protos of micro-bgas (80i/o) pitch .030/.031 | | | | | | 12BGA per assembly | | | | | | | | | | | | The board is a (.062, 4 layers) FR-4 using Dry film | | | | | | Pads .014inch | | | | | | Vias within footprint .020inch | | |
Electronics Forum | Thu Jul 29 15:29:30 EDT 1999 | Earl Moon
| | | | | | | Presently protos of micro-bgas (80i/o) pitch .030/.031 | | | | | | | 12BGA per assembly | | | | | | | | | | | | | | The board is a (.062, 4 layers) FR-4 using Dry film | | | | | | | Pads .014inch | | | | | | | Vias within footprint .02
Blackfox is the industry leader in providing IPC Certifications, Solder Training, Customized Training Programs, and Counterfeit Component Training and Certification.
Training Provider / Standards Setting / Certification / Manufacturer / Consultant / Service Provider
701 Delaware Ave. Unit B
Longmont, CO USA
Phone: 303-684-0135
winsouce.jpg)