Electronics Forum | Thu Aug 27 08:59:31 EDT 2009 | rgduval
Jack, I've heard of it, and reviewed their website; but that's about the limit of my exposure. I'd be interested in impressions after the web demo. I'm assuming you have some knowledge/exposure to Circuitcam. If you'd like to contact me off the s
Electronics Forum | Thu Aug 27 10:14:28 EDT 2009 | jwmcnally
Jack, > > I've heard of it, and reviewed their > website; but that's about the limit of my > exposure. > > I'd be interested in impressions > after the web demo. I'm assuming you have some > knowledge/exposure to Circuitcam. > > If you'd > l
Electronics Forum | Fri Nov 13 04:45:30 EST 2009 | lococost
Hi dave, Sorry to hi-jack the tread a bit, but,we are experiencing some problems with components falling off somewhere in our factory, you made me think about printer settings being an issue. By print print, do you mean a double sweep of the squeeg
Electronics Forum | Mon Jun 21 08:01:38 EDT 2010 | jm
Hello, need some help if anyone has any insight on this issue. Ran first side and ex-ray indicates BGA parts look normal. Ran the second side and now the BGA balls on first side appear to have broken free and moved under part. This board has BGA's
Electronics Forum | Tue Feb 06 16:36:51 EST 2018 | dontfeedphils
For anyone looking back on this post, I ended up figuring out something that will work for my process. Jack up the atomization pressure on the guns, lower material flow, quicker-lighter coats, less time between coats, and more coats. Smooth, even f
Electronics Forum | Tue Jan 24 11:07:41 EST 2023 | poly
Emtimov, what are you using instead? Hand soldering? Is the repeatability due to lacking bottom side fiducials or is the process just inconsistent? We've got a few connectors, something like 20 jacks with 3 pins each on some of our products. Our ma
Electronics Forum | Fri Jul 14 16:29:12 EDT 2000 | Dave F
Awww John, if I typed all that folderol, my spell checker would have gone kaaablewee!!! Most of the stuff I listed is tactical, because I assume most people on the forum are DFM / DFT choir and by the time we get involved, some BIG $$$ consultant ha
Electronics Forum | Fri Jul 14 16:29:31 EDT 2000 | Dave F
Awww John, if I typed all that folderol, my spell checker would have gone kaaablewee!!! Most of the stuff I listed is tactical, because I assume most people on the forum are DFM / DFT choir and by the time we get involved, some BIG $$$ consultant ha
Electronics Forum | Thu Mar 02 13:17:00 EST 2000 | Russ
Jack, a couple of questions first, 1. What pitch are these leads? 2. What are the lead footprint dimensions? 3. Orientation of component? I personally have never had much luck soldering QFPs in the wave unless they are 50 mil pitch or greater, we o
Electronics Forum | Wed Dec 13 10:24:52 EST 2000 | Wolfgang Busko
Hi Jack, I once tried this finish ( without changing any process parameters ) and encountered wetting problems even in the first reflow process. It was thought as cheaper alternative to Ni/Au we use for planarity reasons. Heard of the same problems