Electronics Forum | Tue Aug 31 13:23:37 EDT 2004 | frankracine
Thanks Ken for your reply. Concerning OSP, there are a few negative points that I must considered for our application. I've read all the following points in an Entek document. Never test it. - If you have a miss print and you clean the PCB, the co
Electronics Forum | Wed Jan 11 22:47:31 EST 2006 | davef
We didn't intend to light anyone's fur on fire [get anyone's underwear in a knot, roil the waters, have a cow man] about consultants. The Phil Zarrow wrote a useful paper that could help in evaluating paste. Here read it ... Evaluating Solder Paste
Electronics Forum | Thu May 26 08:52:42 EDT 2011 | davef
Phil Zarrow wrote a useful paper that could help in evaluating paste. Here read it ... Evaluating Solder Paste � Not An Option Contributed by Phil Zarrow of ITM an Independent SMT consulting firm With soldering being the dominant source of assembly
Electronics Forum | Fri Jul 18 03:21:59 EDT 2014 | skipbruce
Hello June The following infomationI find from net for you reference. OSP (Organic Solderability Preservative) 1)Preserves copper surface from oxidation until asse mbly. 2) Very thin coating (100-4000 Angstroms). 3)Applied in a vertical (dip tank
Electronics Forum | Fri Jul 15 16:50:04 EDT 2005 | davef
Few of us here on SMTnet fabricate our bare boards. Most of us are assemblers. So, the solderability of the connections of our boards is a BIG issue with us. Our suppliers protect the solderability of the copper by coating the copper to limit the
Electronics Forum | Mon Feb 09 09:00:17 EST 2015 | jax
Outside the MSD issues stated already (and I cannot provide a exact time not knowing multiple factors like Humidity levels, temps, exposure times, etc...) OSP might be the very worst finish to use in this scenario of side 1 / store on a shelf / side
Electronics Forum | Wed Aug 21 17:44:32 EDT 2002 | davef
Splitting hairs, I expect SIR of all solderability protection, including OSP, to decrease after reflow. What�s more, I expect the SIR of all solderability protection to pretty much decrease over time. The �comb pattern� test specimens meet requirem
Electronics Forum | Fri Sep 10 14:32:49 EDT 1999 | John Thorup
| We have a product, with various PWBs, with over 600 parts each one (We are a low Volume/high mix company with an average component placement per PCB between 250 to 300 parts). This PWBs have 7 to 10, 20 mils pitch parts. We are having problems with
Electronics Forum | Sun Apr 25 12:01:58 EDT 1999 | Earl Moon
| Earl said, in essence: | | | Justin is absolutely right ... | | | | Again, Entek is not much more than a flux coating ... | | | | Metallic coatings protect best, as we all know - especially those electroplated. Those coatings chemical come in ne
Electronics Forum | Fri Jul 30 16:02:49 EDT 1999 | Earl Moon
| | I received a request from customer to assemble ceramic substrate (alumina oxide)that printed with a low temperature Copper thick film conductor (the overglaze layer is polymer). The Copper pads are exposed without any coating. | | This ceramic su