Electronics Forum | Thu Jun 01 21:59:10 EDT 2000 | Ray Chartrand
Does anyone know the current cost to repair a defective solder joint? I seem to recall a number quoted a few years ago of $1.03 per joint with burden of overhead. I've also seen numbers from 50 cents to 50 dollars per joint.
Electronics Forum | Tue Jan 29 13:06:40 EST 2002 | Sergio Vito - Alan Patrick - Cristiano Dick
Dear sirs, We are experiencing problems with lines of lead formed inside the solder joint. In others words, there is a problem with the formation of the solder joint, after analyses on a microscope we can see the lead grouped in some positions. This
Electronics Forum | Tue Sep 04 02:28:17 EDT 2007 | philip_yam
Any one has experience over solder voids in oscillator capacitor joint could result in high phase noise during the digital performances test? The noise signal was gone after solder touch up. What could be the root cause of the high phase noise?
Electronics Forum | Thu Oct 25 08:19:53 EDT 2001 | Dave G
Sounds like somthing disturbed the solder joint while it was @ liquidus. Could the part/leads be moving on the 2cnd pass ?
Electronics Forum | Thu Oct 25 04:52:17 EDT 2001 | Vai
I'm running intrusive reflow. What happened was when the board went thru' the first reflow ( which is secondary side ), at Post reflow, I can see the solder joint quality is very good smooth and shiny. But when we proceed with the 2nd reflow, at Post
Electronics Forum | Tue Sep 10 07:24:13 EDT 2002 | John
I need teoretical info for theme "Matted surface vs solder ball". Is it right that some solder pastes decrease solder balling but give matted surface after reflow? That diference between these pastes and others? Are the matted surface worse solder b
Electronics Forum | Fri Sep 29 15:41:02 EDT 2000 | Dave F
It's easy to reject everything is it? IPC offers excellent training courses for inspectors in interpreting A-610.
Electronics Forum | Wed May 28 11:56:18 EDT 2003 | blnorman
Yes we are using "silicones", but to find this contaminant we were looking for "silicon" the element by SEM/EDS. We use Dow materials and my contact there is checking to see if they have any info.
Electronics Forum | Wed Jan 30 08:30:33 EST 2002 | seto
Hello Dave, Mechanically the conection between the component pad and PCB pad is good (the solder joint is very strong). The problem is associated with poor contact after the use by the customer (vibration, temperature, etc). You can see the pictures
Electronics Forum | Tue Jan 29 20:13:30 EST 2002 | davef
Over-time lead separates from the tin in solder by force of nature [diffusion], but I assume that is not what you are talking about. Please help us understand your question better. Are you saying that the solder does not attach properly to the comp
Our Company handle AOI (Auto Optical Inspection) and SPI (Solder Paste Inspection) Machines.
Equipment Dealer / Broker / Auctions
Hwaseong-si, Gyeonggi-do, Korea
Hwaseong-si, South Korea
Phone: +82-1029254936
.gif)