Electronics Forum | Wed Jul 27 16:27:57 EDT 2005 | GS
It may be you should look for higher TG of Durapol Rgds GS
Electronics Forum | Wed Aug 27 08:00:33 EDT 2008 | cgray
We are using Multicore (MFR 301) from Henkel.
Electronics Forum | Wed Aug 27 14:07:42 EDT 2008 | cgray
Thanks for your experiences.
Electronics Forum | Thu Nov 11 10:51:16 EST 1999 | KenF
Could anyone tell me where I can find some literature/standards describing the dimensions and solder land sizes of all common SMD components available in the market? IPC-SM-782 does provides some but not all. Thanks in advance for any response. Rega
Electronics Forum | Tue Dec 03 11:59:01 EST 2002 | slthomas
We haven't run a profile yet....probably because we're a-feared to. We can't do topside preheating here to any degree because we use an aluminum plate for aligning hundreds of top side through-hole components (pots, switches, buttons, LEDs) that te
Electronics Forum | Thu May 29 18:58:41 EDT 2003 | davef
Lead free solder is bad for the environment, while increasing product costs. The US looked at restricting lead use a few years ago, took no action, and has no plans to enact frivolous legislation like the "greens" have foisted upon the Eurolanders a
Electronics Forum | Tue Jun 03 18:34:22 EDT 2003 | Kris
Hi, There have been other studies where it was found that lead-free soloder joints are more reliable than tin-lead solder joints irrespective of test conditions. In fact the automotive industry has been using Sn/Ag for underhood applications for a
Electronics Forum | Thu Jun 05 06:03:49 EDT 2003 | iman
Japan and Europe are the main champions for the leadfee solder initiative. USA join in due to global political efforts as one of the cub scout leaderships. Military and Automobile industrial-electronics is exempt from the leadfree directive. Reason
Electronics Forum | Wed Jul 27 16:46:48 EDT 2005 | russ
I don't think that you would need to test these. Have you ever seen any evidence of solder sticking to them? We use the same material and never notice anything besides flux staying on the bottom. Would the lead absorption if any even be of a concer
Electronics Forum | Sat May 15 11:27:26 EDT 2010 | davef
We'd expect both OSP poor wetting and improper reflow recipe to show-up in more places than just this one component. But if those are the only choices, we'll go for 'wrong solder paste.' Ooops, that's not one of the choices. Ok, OK, we'll take poo