Electronics Forum | Tue Jun 29 14:42:55 EDT 2004 | davef
You're correct, for every dumpster full of paper written about solder, there's a sentance written about fluxes. There's dribs and drabs about fluxes in most of the soldering books [ie, Manko, Klein-Wassink, Judd, Strauss, etc] and most of that is ve
Electronics Forum | Thu Jan 29 17:04:43 EST 2009 | jeffjarmato
I run two different waves here one with SAC305 with aqueous flux the other with SN100C and No clean flux. Does anyone see any issues with running product through either machine of course after changing the Flux type? I also only use SAC305 alloy for
Electronics Forum | Mon Jul 12 11:35:27 EDT 2004 | Pierre RICHARD
Here are some answers to my questions after a good research. I also added more definitions that could help understand this esoteric language used in assembly, specially surrounding fluxes and their use. In blue italics are comments and extracts from
Electronics Forum | Wed Jul 07 17:55:18 EDT 2004 | davef
Another thought, why not contact a flux supplier that is able to give you the background information you seek? For instance: Daniel Werkhoven; Interflux Electronics/Belgium [ http://www.interflux-electronics.com ] [We have no relationship, nor rec
Electronics Forum | Fri Aug 24 09:29:08 EDT 2007 | jgrootkoerkamp
Solder balls with wave soldering can have different causes. The two most important are the solderresist and the flux. I have similar problems, after changes the flux type 90% off all solderballs are gone. KR, Joris Groot koerkamp
Electronics Forum | Fri Aug 24 12:39:59 EDT 2007 | hussman
I would say no, unless your machine is in extremeconditions. You may want to check your flux / preheat out as well. If you are leaving a lot of flux on the board at wave, it may be boiling - which can cause solder balls.
Electronics Forum | Mon Nov 02 14:45:25 EST 2015 | stevezeva
Hi there! If they are just standard headers there's a company called Teka that makes headers and socket headers with solder preforms in them. They call it "Solder Bearing Lead Technology" You can drop them in the board and reflow them just like SMT p
Electronics Forum | Wed Sep 25 06:56:16 EDT 2002 | CH
U may check your profile ramp rate. The flux may evporated and look like cold joint
Electronics Forum | Fri Aug 26 14:15:16 EDT 2005 | David
Where could I find more information regarding the double sided reflow and flux problems with white tin?
Electronics Forum | Fri Aug 24 12:25:32 EDT 2007 | grics
What about when using noclean and alcohol based fluxes? Could humidity still cause issues?