Electronics Forum | Thu Nov 08 16:02:28 EST 2007 | ck_the_flip
We've got lots of connectors at my place of employment like this. What I do is... I run these "slower than molasses in January" - we're talkin' 2 Ft/Min. conveyor speeds. Obviously this will have an effect on your thermal profile so compensate acco
Electronics Forum | Sat Nov 24 15:44:28 EST 2007 | mika
Hi DaveF, I had a short look into the Nr1. IMPACT OF MICROVIA-IN-PAD DESIGN ON VOID FORMATION Most interesting reading, but one thing though, I could not find any information about the oven profile. Just a picture of it. My question is of about the
Electronics Forum | Wed Nov 07 17:57:01 EST 2007 | jmelson
OH! He he, St. Louis! I have recently acquired a very good P&P machine, and am in the St. Louis area. I got the machine primarily for my own manufacturing, but there is plenty of time available on the machine. If you'd like to see how the process
Electronics Forum | Mon Nov 12 09:22:41 EST 2007 | devajj
BTW, The surrounded QFN fine pitch terminals > should have the normal aperture reduction of 7 % > in case of RoHS Senju solder paste. This works > for our Telecom customer. > > The vias in the > ground pad will be somewhat filled with solder >
Electronics Forum | Fri Nov 16 08:33:46 EST 2007 | rgduval
For RoHS assemblies, we're spec'ing at least FR-406 for the higher Tg. We're currently requesting our customers to use ENIG finish, as we've had better luck with assembly in our process; but we're currently experimenting wtih lead-free HASL. As far
Electronics Forum | Mon Nov 19 09:34:50 EST 2007 | bbarton
Real Chunks...Yes, that's the most glaringly obvious defect in the short term (you'll probably find it on your production floor if it's really bad) but you may find that everything looks good short term only to have a high level of customer returns..
Electronics Forum | Tue Nov 20 20:26:54 EST 2007 | davef
Peter: The above link to the the picture of the assembly is broken. Comments are: * Yes, RTV is completely useless for applications like you describe. Epoxy is a much better choice. * Dave G, in an archived thread on SMTnet, talks about using 3M Jet
Electronics Forum | Mon Dec 03 10:22:11 EST 2007 | pms
The PCB's are supplied by the customer. No options. The BOSS say's get it done, make it work, I don't want to hear it. My BOSS is a psychotic idiot. The printer is a DEK with no options for manual fiducial over-ride. I think my idiot BOSS wrote the
Electronics Forum | Mon Dec 17 19:01:45 EST 2007 | bbarton
As someone with a LOT of experience with the "low cost" alternative alloys, primarily SACX, I have one simple question....Are these shorts a new phenomena? WAS your process in control, and all of a sudden it's not? If the answer is YES, take a look a
Electronics Forum | Tue Dec 18 10:08:16 EST 2007 | bbarton
Drill a hole through the board (or the BGA) and set a thermocouple into the center of the device (in the X Y and Z dimensions) and run your profiler through the oven until you get the temp you need in the center of the BGA. Attach a second thermocoup