Electronics Forum | Thu Jun 04 11:23:44 EDT 1998 | Frank S
If you could measure and chart 3 variables in my process, what would they be? The boards that I produce are on panels that are 12up and 2x4 up. All boards are single sided paper base w/o plated thru holes. They are on scored panels that measure 7"
Electronics Forum | Thu Jun 04 11:57:59 EDT 1998 | Pete M
Be more specific on your problems? | If you could measure and chart 3 variables in my process, what would they be? | The boards that I produce are on panels that are 12up and 2x4 up. All boards are single sided paper base w/o plated thru holes. The
Electronics Forum | Tue May 26 20:24:39 EDT 1998 | Dave F
| Does anybody know a (if possible low-cost) system | which can travel with the PWBs through a reflov oven | (like some temperature profile loggers) for measuring | the residual oxygen? My problem is, it is a batch oven | which does not allow to h
Electronics Forum | Fri Aug 10 09:57:24 EDT 2001 | John
We are an OEM automotive electronics supplier and began using SMT in our products a couple of years ago. We use a glue and wave process, and one of our main issues has been our glue dispensing process. We have a Camelot 3800 machine, and we have be
Electronics Forum | Thu Oct 25 16:48:29 EDT 2001 | Cemal Basaran
We can inspect and measure strain field in anything larger than 320nm with Laser techniques we have. We can do this measurements during fatigue testing. Of course thick intermetallic region as a solid region is a problem due to the fact that you ha
Electronics Forum | Thu Apr 04 16:38:51 EST 2002 | davef
Equipment companies like to talk about �accuracy� and �repeatability�. These measures provide limited information. Flaws of the measure aside, some printer companies have begun to report Cp. * DEK ELA: Cp = 1.33 @ �0.025mm * DEK 265: Cp = 1.6 @ �0.0
Electronics Forum | Tue May 14 08:04:58 EDT 2002 | robbied
Hi. Does anyone out there know of a way to calculate the surface area of populated PCB's? We build many different types, and until now have been using a water displacement method, which I believe to be fundamentally flawed. Our technique is to drop a
Electronics Forum | Mon Jun 17 15:04:08 EDT 2002 | genny
I think I had my units wrong in my previous post - that blueprint job was 6 years ago and fading fast. My level of 700 would have the same units as Dave's level of 1000. This is the metric measurement of lux, vs the imperial footcandles. fc to lux
Electronics Forum | Mon Aug 26 20:35:08 EDT 2002 | davef
There are no industry standards for eutectic solder-paste in conjunction with the life span of solder-paste. Whatever that is. Speaking of that ['whatever that is.'], what do you mean by �life span of solder-paste�? Is that: * Shelf life? * Workin
Electronics Forum | Wed Sep 11 23:20:44 EDT 2002 | scottefiske
Profiles are absolutely the first course of action to validate. A few additional questions would be: * Moisture can cause warping as well, verify the manufacturers recommended handling procedures were followed. * Where is the suspect BGA located