Electronics Forum | Wed Jul 14 10:58:25 EDT 1999 | Upinder Singh
| | Hi All, | | Does any one experienced the solder on gold finger after | | reflow. Its about 5 to 8 mils diameter . | | We'd clean the entire screen printer, mounter & reflow as well, | | but doesn't help much. | | | | | Mr Kong..... | | Solder
Electronics Forum | Tue Jul 13 13:51:51 EDT 1999 | Earl Moon
| | | Hi all , | | | | | | We are trying to implement the micro-BGA technology at our plant. I need the clarification to the following points: | | | | | | 1. Is underfill required for micro-BGAs? | | | | | | 2. What type of stencil apertures are t
Electronics Forum | Tue Jul 13 07:57:27 EDT 1999 | Mark Quealy
| | | | I am looking for suppliers of ESD floor coverings. I currently have ESD carpet and I would like to replace them with ESD Tile. Help Me | | | | | | | | MD Cox | | | | | | | | Try a search in the archives. A while back someone asked for
Electronics Forum | Thu Jun 24 12:43:08 EDT 1999 | Earl Moon
| | Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody h
Electronics Forum | Fri Jun 25 12:01:49 EDT 1999 | Earl Moon
| | Dear John/Earl | | | | Thanks for your clarifications. To me also the problem does not seem to be linked with the PCB. The Pre heater temp. is set at | | 450 degree C. We are using Alpha Aq. cleanable flux. Can you elaborate on the Desired
Electronics Forum | Sun Jun 20 06:30:49 EDT 1999 | Scott Cook
| Do anyone have any experience on assembling high frequency product, 1.8GHz or 2.4GHz. | | In our production line, we manufacture 1.8GHz product with using no clean paste (RMA type) for reflow and no clean wire for rework. In our functinal test,eit
Electronics Forum | Fri Jun 18 11:33:16 EDT 1999 | Brian wycoff
| | first of all what is the technical term for the small amount of solder on a plated pad. we are getting poor screen printing gasketing on a 20 mil qfp due to this solder not being even or too high in spots and not covering the length of the pads.
Electronics Forum | Wed Jun 16 10:44:04 EDT 1999 | Clifford Peaslee
Brian, Thanks for your concern, and maybe there is fear that we are trying to mislead people, which is not true. We do not have the server in house here in Portland, Maine. It is in Fort Lauderdale, Florida, at Advances.com. We are sharing a netw
Electronics Forum | Tue Jun 15 12:03:27 EDT 1999 | Dave F
| Has anyone had issues where bottomside double reflowed smt has fallen off in the wave when using voc-free flux? I have verified the hotter profile was not the issue by using an alcohol based flux with no problems.This voc-free flux is also not caus
Electronics Forum | Tue Jun 08 12:49:41 EDT 1999 | Dave F
| Hi,my master | How to iron out such soldering bridge with below conditions: | 1.The component(Harness)lead pitch is 2.0mm,the lead length is 3.2mm. | 2.PCB width is 1.6mm.Pad size is 1.65mm.Its a single copper PCB | 3.using spraying fluxer and n