Electronics Forum | Thu Jul 28 09:23:48 EDT 2005 | fctassembly
300 million boards to date). I also have some reliability data for joints made with these 2 alloys wave soldered and then repaired with both. All of these results look good. The issue we see is mixing SN63 with any of the lead free alloys. Sn63 wave
Electronics Forum | Wed Aug 10 21:47:17 EDT 2005 | Geoff
Nihon superior could not provide any written aprovals but In asia.......... Sony- SN100C in use for car and home audio applications. Panasonic- SN100C in use for DVD, VCR, battery, and home appliances applications. Pioneer- SN100C in use for everythi
Electronics Forum | Wed Mar 08 11:59:10 EST 2006 | c_nguyen
Hi Folks, Does anyone know whether the following machine can do Lead-Free BGA rework? Also how much you would recommend to pay for this machine? Please advice! Your input is greatly appreciated. ================================================ Air-Va
Electronics Forum | Wed Mar 08 11:59:18 EST 2006 | c_nguyen
Hi Folks, Does anyone know whether the following machine can do Lead-Free BGA rework? Also how much you would recommend to pay for this machine? Please advice! Your input is greatly appreciated. ================================================ Air-Va
Electronics Forum | Wed Aug 03 10:14:59 EDT 2005 | Wonderboy
With oven temps rising due to Lead-Free Processing, I'm looking for some information on high temp Reflow Oven lubricants. I've found some info in the Fine SMTnet Archives on Chain Lubricants, (Mostly Synthetic Motor Oils), but I'm wondering what othe
Electronics Forum | Fri Sep 02 05:17:54 EDT 2005 | pyramus
I have another question can anybody assist me. Is there any specific procedure or guidelines that need to be followed for handling PCB (OSP & Immersion Tin)? Moisture Sensitive Devices? or how about throw-out or left over parts? Is there any paste h
Electronics Forum | Sat Oct 01 11:48:45 EDT 2005 | Hiram
Hello everybody, We are in the process of implementing NC process on the wave solder. We have a Sonotek XL fluxing system. Any ideas out there? Solder used: SN100C Flux options so far: 264-5 flux, 270WR VOC-free 9both from AIM solder) The flux ch
Electronics Forum | Mon Oct 03 12:11:18 EDT 2005 | PWH
Soon we will be manufacturing board assemblies on our SMT lines that will utilize both lead and lead free water soluable solder pastes. I have read some discussion about change-over from lead to lead-free jobs related to machine cleanliness, etc. H
Electronics Forum | Fri Oct 07 09:18:39 EDT 2005 | russ
If you're using non-lead free parts then you don't have a pbfree assembly so why worry about marking it anyway? We apply this artwork after the assembly has been completely engineered for lead free. Artwork can be covered up with mask or whatever if
Electronics Forum | Sun Oct 09 08:28:04 EDT 2005 | davef
First, no one knows very much about the relaibility of Pb-free assemblies, much less Pb-free solder with Pb-bearing components. Second, we do know that Pb-free components work with PB-bearing solder. Third, based on comparison laboratory testing,