Electronics Forum | Fri May 28 17:30:35 EDT 1999 | Dave Clements
I discovered that we have some gold plated (30 mico in.) through hole connectors which were Paste In Hole soldered (60 sec at reflow) on a HASL PCB. Do we have an embrittlement reliability issue? The calculated volume % of gold in the joints is about
Electronics Forum | Fri May 28 17:44:51 EDT 1999 | Glenn Robertson
| I discovered that we have some gold plated (30 mico in.) through hole connectors which were Paste In Hole soldered (60 sec at reflow) on a HASL PCB. Do we have an embrittlement reliability issue? The calculated volume % of gold in the joints is abo
Industry News | 2016-11-30 14:47:45.0
ACI Technologies invites you to download a free copy of its very popular e-booklet, “Failure Analysis Techniques for Electronics” from its Website store, which is located at http://store.aciusa.org/Failure-Analysis-Techniques-for-Electronics-Digital-Download-P181.aspx
Industry News | 2021-04-13 17:37:07.0
Gold plating dissolves rapidly during soldering and can result in gold embrittlement. This tech paper examines how to re-condition electronic components prior to soldering.
Technical Library | 2014-08-07 15:13:44.0
Gold embrittlement in SnPb solder is a well-known failure mechanism in electronic assembly. To avoid this issue, prior studies have indicated a maximum gold content of three weight percent. This study attempts to provide similar guidance for Pb-free (SAC305) solder. Standard surface mount devices were assembled with SnPb and SAC305 solder onto printed boards with various thicknesses of gold plating. The gold plating included electroless nickel immersion gold (ENIG) and electrolytic gold of 15, 25, 35, and 50 microinches over nickel. These gold thicknesses resulted in weight percentages between 0.4 to 7.0 weight percent.
Technical Library | 2022-08-08 15:06:06.0
Selective soldering has evolved to become a standard production process within the electronics assembly industry, and now accommodates a wide variety of through-hole component formats in numerous applications. Most through-hole components can be easily soldered with the selective soldering process without difficulty however some types of challenging components require additional attention to ensure that optimum quality is maintained. Several high thermal mass components can place demands on the selective soldering process, while the use of specialized solder fixtures, or solder pallets, often places additional thermal demand on the preheating process. Fine-pitch through-hole components and connectors place a different set of demands on the selective soldering process and typically require special attention to lead projection and traverse speed to minimize bridging between adjacent pins. Dual in-line memory module (DIMM) connectors, compact peripheral component interface (cPCI) connectors, coax connectors and other high thermal mass components as well as fine-pitch microconnectors, can present challenges when soldered into backplanes or multilayer printed circuit board assemblies. Adding to this challenge, compact peripheral component interface connectors can present additional solderability issues because of their beryllium copper base metal pins. Key Terms: Selective soldering, drop-jet fluxing, sustained preheating, flux migration, adjacent clearance, lead-to-hole aspect ratio, lead projection, thermal reliefs, gold embrittlement, solderability testing.
ACI Technologies Inc. (ACI) is a scientific research corporation dedicated to the advancement of electronics manufacturing processes and materials for The Department of Defense and industry. This video provides an overview of our commercial service
SMTnet Express, August 7, 2014, Subscribers: 23058, Members: Companies: 13975, Users: 36604 Gold Embrittlement In Lead-Free Solder. Craig Hillman, Nathan Blattau, Joelle Arnold, Thomas Johnston, Stephanie Gulbrandsen; DfR Solutions , Julie Silk
Surface Mount Technology Association (SMTA) | https://www.smta.org/knowledge/proceedings_abstract.cfm?PROC_ID=5255
) when the solder gold content exceeds 5% by weight. Controlling the component gold plating thickness as well as the soldering process temperature and time can prevent gold embrittlement