Electronics Forum | Mon Nov 12 01:18:29 EST 2007 | sin4d
Hi, ALL I experience some QFP with wetting issue on the heel of the lead. There is no fillet wetting on the heel which causes reject bt the customer, but not all the QFP. Could anyone pls help what is the causes of this problem, it is due to oxidati
Electronics Forum | Tue Sep 14 21:03:42 EDT 2010 | genesan
Hi Sir, The diameter of the aperature is 17mil and thickness 6mil and since we are using Solder Paste Inspection i believe that should have a good paste deposit on this pad.Let say if no good paste it will more create insufficient solder which X-RAY
Industry News | 2011-09-14 12:04:43.0
The SMTA announced a session on QFN Assembly and Reliability will take place on Tuesday, October 18 during their annual conference, SMTA International, in Ft. Worth, Texas. Andrew Mawer of Freescale Semiconductor will chair the session and Viswam Puligandla, Ph.D., Nokia (Retired) will co-chair.
Industry News | 2013-09-10 12:18:26.0
The Surface Mount Technology Association (SMTA)'s Intermountain Chapter will hold its annual technical symposium on September 19 at the University of Utah in the Warnock Engineering Building, Salt Lake City, Utah.
Technical Library | 2020-11-24 23:01:04.0
The miniaturization trend is driving industry to adopting low standoff components or components in cavity. The cost reduction pressure is pushing telecommunication industry to combine assembly of components and electromagnetic shield in one single reflow process. As a result, the flux outgassing/drying is getting very difficult for devices due to poor venting channel. This resulted in insufficiently dried/burnt-off flux residue. For a properly formulated flux, the remaining flux activity posed no issue in a dried flux residue for no-clean process. However, when venting channel is blocked, not only solvents remain, but also activators could not be burnt off. The presence of solvents allows mobility of active ingredients and the associated corrosion, thus poses a major threat to the reliability. In this work, a new halogen-free no-clean SnAgCu solder paste, 33-76-1, has been developed. This solder paste exhibited SIR value above the IPC spec 100 MΩ without any dendrite formation, even with a wet flux residue on the comb pattern. The wet flux residue was caused by covering the comb pattern with 10 mm × 10 mm glass slide during reflow and SIR testing in order to mimic the poorly vented low standoff components. The paste 33-76-1 also showed very good SMT assembly performance, including voiding of QFN and HIP resistance. The wetting ability of paste 33-76-1 was very good under nitrogen. For air reflow, 33-76-1 still matched paste C which is widely accepted by industry for air reflow process. The above good performance on both non-corrosivity with wet flux residue and robust SMT process can only be accomplished through a breakthrough in flux technology.
Technical Library | 2017-08-17 12:28:30.0
At SMT assembly, flux outgassing/drying is difficult for devices with poor venting channel, and resulted in insufficiently dried/burnt-off flux residue for no-clean process. Examples including: Large low stand-off components such as QFN, LGA Components covered under electromagnetic shield which has either no or few venting holes Components assembled within cavity of board Any other devices with small open space around solder joints
Lyra Reflow Oven is a soft soldering that realizes the mechanical and electrical connection between the solder ends of surface mount components or the pins and the printed board pads by remelting the solder paste pre-distributed on the printed board
#Xray#Inspection#SEC Nano-focus Tube of 200 nano resolution which is specialized for sub-micron defects of Semiconductor Packaging, Wafer Level Packaging(WLP). -Non-destructive Analysis System -High-Resolution Image with Dual Type CTs -Application
Career Center | Oldsmar, Florida USA | Maintenance,Production
Job Description: • Uses microscope to verify correct part placement and orientation, manually align parts before soldering and perform post re-flow inspection and touch-up. • Able to identify and touch up poor wetted solder joints, solder voids / i
Career Center | Oldsmar, Florida USA | Engineering,Maintenance,Production
Job Title: Assembler 2 – IPC 610 – 1st Shift Address: 3655 Tampa Rd, Oldsmar FL 34677 Duration: 1 year Pay Rate: $15-$18 Hours: 9/80 schedule Monday – Thursday 6:00AM – 3:30PM, Friday 6:00AM to 2:30PM Job Description: Use microscope to verify
Career Center | Botevgrad, Sofia Bulgaria | Engineering,Production,Quality Control,Research and Development,Sales/Marketing
AOI - Omron RNS/RNS_ptH, VI3000, Marantz 22X IPC-610D Class 3, Pb/Pb free process, 5S, FMEA, MSA, PPAP, SPC, CPK, 6Sigma, lean manufacturing, Quality management, ISO/TS 16949 ,ISO 9001,ISO 14 001
Career Center | Botevgrad, Sofia Bulgaria | Engineering,Production,Quality Control
AOI - Omron RNS_ptH, RNS-LS, VT-WIN2 VI3000 Marantz 22X IPC 610D certified ISO 9001-2008, etc automotive standards ROHS