Electronics Forum | Wed Jan 09 17:14:48 EST 2002 | mregalia
Do you bond with Al or gold wire? What happens if the Ni is over 150 microinches? Thickness of nickel is one those things that we have not been consistent with. The industry seems to pretty much universally call for 100-200 microinches. Our old board
Electronics Forum | Thu Jan 12 20:11:25 EST 2012 | davef
Isola water pressure. Between a 210°C normal tin lead cycle and a 250°C lead-free assembly cycle, the vapor pressure doubles. Reflow temperature [*C]||Vapor pressure of water [psi] 150||100 200||225 210||260 220||320 230||400 240||480 250||580 300||1
Electronics Forum | Thu Jan 07 17:25:24 EST 2016 | hegemon
Not sure how anyone could pretend to "ballpark" a cost for a board, regardless of size, especially in small quantities. You might need 10 assemblies, but the MOQ for your main component might be 100, 200, 500, 5K pcs. Makes me laugh every time I
Electronics Forum | Wed Feb 03 16:45:20 EST 1999 | Mark Henebry
Does anyone know if I will have problems soldering surface mount components to an all hard gold plated PC board. We want to use hard gold similar to gold used for edge fingers because our customer is concerned about wear and conductivity of connector
Electronics Forum | Thu Apr 01 11:53:33 EST 2004 | russ
You may want to tack a coup[le of leads first, making sure that the component is fully seated against the PCBA. Or what we do is apply solder to the E-Pad and the lead pads and then hit it with a "heat gun" until the solder melts on the E-Pad and th
Electronics Forum | Thu Apr 19 20:21:07 EDT 2012 | eadthem
You might keep a eye on SMT auctions, Sometimes you can get a good deal. As long as you get the feeder for less than 100-200$ each at auction/ up to 500$ each for a dual lane, you can be assured that you can fix it to fully working if its broken
Electronics Forum | Fri Aug 19 08:00:13 EDT 2016 | eplankey
I’ve been tasked with acquiring both pricing and specification information on potential X-Ray units. If possible I would like to gather information on both low-end and high-end units. Here is some information on our facility. I have been to facili
Electronics Forum | Sat Dec 12 04:21:13 EST 2009 | nkohler
Hello, We use SJ50 serie AOIs. I made a program which watches the .dat file and if an algorithm changes then my program makes a log file from the parameters of the modification. I know some numbers are which parameters, but I don't know all. I write
Electronics Forum | Fri Mar 16 11:52:31 EST 2001 | J.D. of Panasonic
Ed, You certainly are ready for some equipment. I noticed in your message that you mentioned cost three times. So it is a very big issue to you. What everything depends on is where you see your company going in the next few years. Do you want
Electronics Forum | Wed Feb 03 18:36:47 EST 1999 | Earl Moon
| Does anyone know if I will have problems soldering surface mount components to an all hard gold plated PC board. We want to use hard gold similar to gold used for edge fingers because our customer is concerned about wear and conductivity of connect