Electronics Forum | Tue Dec 12 20:37:31 EST 2000 | narasimhan68
Hi, I would like to know the details about getting work permit for US. Presently I am working in India in SMT area over 9 years. If somebody can give some info about will be appreciated for my career growth. narasim
Electronics Forum | Mon Sep 24 18:03:43 EDT 2012 | rmazenha
Hi, i am using AIM 264-5 No Clean flux for soldering alpaca pieces on PCB boads, but i am having problems: poor filling and no solder. I am using SAC 305 lead free solder. I have tried to change flux pressure, time, ammount as well solder speed an
Electronics Forum | Mon Nov 01 15:47:21 EST 1999 | Jim Snipes
Dave thaanks for your quick reply. The flow through probelm exists on several component, Examples; small Tan electolic caps.,electrolic epoxy caps. and one specfic lad on a resistor network. I have veried conveyor speed and readjusted heat sett ings
Electronics Forum | Thu Mar 04 12:00:56 EST 2004 | tryn
I am looking at two different type fluxes, Kester 951nc and AIM 264-5nc. The two seem to be comparable, but the Kester is listed as an ORL0 and the AIM as a ROL0. My product builds are all military and I have been dictated to use only ROl0 flux. I kn
Electronics Forum | Sat Oct 01 11:48:45 EDT 2005 | Hiram
Hello everybody, We are in the process of implementing NC process on the wave solder. We have a Sonotek XL fluxing system. Any ideas out there? Solder used: SN100C Flux options so far: 264-5 flux, 270WR VOC-free 9both from AIM solder) The flux ch
Electronics Forum | Fri May 26 10:17:21 EDT 2006 | pjc
Here are settings for a Vitronics SMR500 oven for Indium Corp. 5.1 No-Clean Pb Free solderpaste, the product profiled was of medium thermal mass: RTS, Temp C 120, 170, 195, 248, 264, conveyor speed was 43cm/min (17"/min.) Peak temps were reached in
Electronics Forum | Fri Nov 20 01:00:50 EST 2015 | anilwagh
I am looking below parts of CP4-2. 1)1P150E-24-2 3)2MMB500U-01-1 3)3MMB50-4-1 4)4P300E-05-1 5)CACR-SR03BC IKS-Y264-1 6)CACR-SR10BC 1KS-Y262-1 7)CACR-SR44 BC 1BF-Y279-1
Electronics Forum | Wed May 22 12:00:13 EDT 2019 | gregoireg
Thanks. It starts to make sense. There is a formula at the bottom of this page: http://www.circuitinsight.com/programs/50456.html It says: Stencil Thickness = 2.64mil + 0.0831 * pitch of component in mil. for 1.13mm, that gives exactly 0.16mm. So,
Electronics Forum | Mon Aug 22 09:01:09 EDT 2005 | iwan
Well guys, I just buy a brand new solder paste softener Malcom type SPS2, I've tried with this with this viscosity result. I Use Almit Solder Paste Lead Free LFM-52X 1 min : 264 pas. 2 min : 272 pas. 3 min : 277 pas. I use standard for Viscosity 20
Electronics Forum | Mon Mar 07 16:36:37 EST 2011 | remullis
I have been working on collecting data all day today. We are a OEM so our RMA and QA system is tied together. I have taken this data and broken it down by part type and individual boards. We had 264 (defects/rma returns) of that, 88 were NO Faults. O