Electronics Forum | Wed Sep 28 03:58:05 EDT 2011 | Jacki
Hi All My company is doing PCB assembly.To save cost, we change our wave solder bath from SnAg to SAC 305. What is the pros and cons for using SAC 305 solder? And,will affect to our quailty? Thanks in advance.
Electronics Forum | Tue Oct 18 19:29:06 EDT 2011 | warwolf
hey Jacki we are looking at going from SAC305 to SN100C, if your looking to save cost it's a cheaper option. have a look into it.
Electronics Forum | Thu Nov 10 21:25:49 EST 2011 | zaza
Hi Jacki, You should change to SN100C instead of SAC305. It give you excellent quality: 1. Can reduced solder short & icicles problem. 2. Very shinning solder joints. Rgds, Zaza
Electronics Forum | Sat Nov 26 04:48:55 EST 2011 | rajeshwara
Better you alos take look at Cookson Alpha SACX0807 / SACX0107 alloy
Electronics Forum | Sat Nov 26 04:49:00 EST 2011 | rajeshwara
Better you alos take look at Cookson Alpha SACX0807 / SACX0107 alloy
Electronics Forum | Tue Oct 25 11:07:19 EDT 2011 | davef
While you're waiting for others to reply, search the fine SMTnet Archives to find threads similar to your posting. For instance: http://www.smtnet.com/Forums/index.cfm?fuseaction=view_thread&Thread_ID=9674
Electronics Forum | Wed Nov 16 12:54:00 EST 2011 | Shean Dalton
Jacki, your original post was regards to wave solder bath. With solder bar, there is no flux and you do not need to look for WS Sn100C. Sn100C is only a metal alloy. Regards, Shean
Electronics Forum | Tue Nov 15 22:27:21 EST 2011 | Jacki
Hi Zaza Thanks. Again, very appreciate if you advise me where I can get the SN100C solder bar that is water soluable. Now I'm checking Nihon Superior(Singapore) whether they have or not. As our customer's preference, we have to use the watersoluab
Electronics Forum | Fri Mar 03 13:44:36 EST 2006 | Jon Provost
We switched to Sn100C on 2 waves and kept one with SAC305. The SAC305 will be converted to SN100C as soon as the Aim rep. delivers it next week.
Electronics Forum | Mon Jan 02 08:54:58 EST 2006 | aj
has anyone used or trialed the SACX from Alpha, from reportes and studies carried out it seems that its a go between SAC305 and SN100.