Electronics Forum | Wed Apr 14 13:39:48 EDT 2004 | procon
Also check out AIM's NC368 / LF218 www.aimsolder.com
Electronics Forum | Thu Apr 15 15:32:27 EDT 2004 | russ
Where does the 260 Deg. C spec. come from that you mention?
Electronics Forum | Wed Apr 14 12:27:49 EDT 2004 | pjc
try Indium Corp's SMQ230. http://ncsmq230.indium.net/ Peak "on board" temps of 229C with good wetting have been obtained.
Electronics Forum | Thu Apr 15 14:36:06 EDT 2004 | Ted
I need solder that has a solidus temp. of approximately 260C so that when sent through a second reflow of 260C the solder doesn�t become liquidus. However, I need the max reflow to be less that 300C because of the substrate.
Electronics Forum | Thu Apr 15 15:54:13 EDT 2004 | pjc
You ned to speak with an apps engineer from a paste supplier that can go through their alloys. I know Indium has such alloys. Any vendor should be able to supply you a list of alloys avbl in NC paste with their liquidous points.
Electronics Forum | Thu Apr 15 20:48:57 EDT 2004 | Ken
Tin antimony mp = 236-240C 80Au / 20SN mp = 280C sn25 Ag10 sb = 365C There are very few high temperature service alloys. how about filling a 1400lb pot with 80% Gold! What is the application?
Electronics Forum | Wed Apr 14 12:23:59 EDT 2004 | Ted
Hi everyone! I am looking for a lead-free solder that will survive a customer reflow of 260C. I am currently using SN10/Pb88/Ag02 but the reflow temperature is to high (320C) for the FR4 boards that we have. I know there are higher temp FR4 boards
Electronics Forum | Wed Apr 14 20:24:48 EDT 2004 | Ken
What do you mean the solder must "survive" 260C? What is your target temperature? Is it dictated by a component, the substrate or the solder alloy? Do you require a eutectic alloy? If not, the selection of alloys grows. (these are from memory...n
Electronics Forum | Fri Jun 22 11:54:47 EDT 2001 | jdtpfacreate
OEM Boy, This is an excellent question. Since I am on the "I-want-to-sell-you-equipment-side" I do not have the hands-on experience that you do but, I do have a many engineers back at our factory who have dedicated their lives to these issues.