Electronics Forum | Tue Oct 02 12:56:41 EDT 2001 | Scott B
We have come across this where the operator was using thin gauge solder wire (more suited to fine pitch SMT soldering) to form large solder fillets (power connections or sheild cans). We found that the operator was feeding large amounts of solder wir
Electronics Forum | Mon Oct 01 16:55:27 EDT 2001 | davef
I agree. Poor soldering technique is the most straightward way of creating solder balls during hand soldering operations.
Electronics Forum | Sun Sep 30 00:54:06 EDT 2001 | chinaman
Has anybody heard about solder wires for rework with a V-notch in order to avoid solder balls which might be caused by shooting flux when getting hot. The notch is as deep to reach the core so that the flux can expand easily. I can imagine the effect
Electronics Forum | Mon Oct 01 03:46:57 EDT 2001 | wbu
Have never heard of solderballs during rework using solder wire. Noticed the tendency to have little balls of flux with too hot iron and lots of solder used for shields or massive cables to be connected. Seems to me a question of believe if it does
Electronics Forum | Thu Jan 14 15:36:23 EST 2010 | tds
JBC Tools has a wire solder feed solder iron. You can control how much is dispensed to the tip. I have sold several of these to customers soldering wires in to terminals. The hand piece is bigger than the typical solder iron but it beats the alter
Electronics Forum | Fri Jan 29 02:59:02 EST 2010 | szsummersun
hi peter, i have experience with manual soldering iron using automated wire feed,please email to me about it in detail,thank you.email:steven@ludeecircuits.com
Electronics Forum | Wed Jan 06 14:34:20 EST 2010 | ppwlee
Hi, Has anyone have experience with manual soldering iron using automated wire feed? I am looking at poke yoke manual soldering 5 pins LCD and wondering if there are ways to control the volume of the solder applied to the board to minimize missing s
Electronics Forum | Wed Jan 23 06:12:36 EST 2019 | tirthkar8980
Dear Team, Need help, we are trying to make urea core solder wire but the problem is some time core remains partially empty no urea filling in solder wire. please help me how to solve this problem. thank you, Tirthkar
Electronics Forum | Thu Jan 29 09:18:36 EST 2015 | davef
Nichrome, manganin, phosphor bronze etc are easy to solder ... the hard part is removing the corrosion * Manganin: 86% copper, 12% manganese, 2% nickel. Often, it's used in making cryogenic measurements, due to its low heat loss. * Select a flux for
Electronics Forum | Fri May 19 10:41:50 EDT 2017 | solderingpro
To be clear: Is the break occurring at the solder joint location? Also, can you advise what solder chemistry you are currently using?