Electronics Forum | Tue Apr 06 10:30:48 EDT 1999 | Scott Davies
Tony Although I agree in principle with Dean that 45 Degrees would be ideal, most of the squeegees I have worked with have been 60 Degrees to the stencil surface. This seems to work best with metal squeegees when printing HASL boards, because the sl
Electronics Forum | Wed Apr 07 11:42:16 EDT 1999 | Tony A
| Tony | | Although I agree in principle with Dean that 45 Degrees would be ideal, most of the squeegees I have worked with have been 60 Degrees to the stencil surface. This seems to work best with metal squeegees when printing HASL boards, because
Electronics Forum | Thu Jun 13 21:44:21 EDT 2002 | jkhiew
Hi all, * Defect : termial to terminal touching btw two melfs body that created short circuit. * Clearance : 0.8mm btw two melfs body. * Size melf : diameter=2.4mm to 2.7mm, length=4.8mm to 5.2mm * Stencil opening : "v" shaped to minimise component
Electronics Forum | Wed Nov 01 08:17:39 EST 2000 | Adam
we have a variety of products which we build and manufacture and build on our site, 90% of which go over the wave solder. What I would like to know is when designing a WSC how do I know what the correct angle of the aperture is in relation to the wav
Electronics Forum | Thu Jan 22 20:10:19 EST 1998 | Raymond
I have the following questions with regards to the solder printing stencil design : 1) Is the Electro-polish process recommended for laser cut stencil ? 2) Should the aperture walls be slanted at an angle or straight wall, i.e. trapezoidal openin
Electronics Forum | Sun May 28 08:21:52 EDT 2000 | Sal
Can't agree more than moving over to Homebase apertures, But ensure that the cut back angle is correct,to acute of and angle will leave you with an inadequate contact area fot the terminations on the chip components and you will start seeing insuffic
Electronics Forum | Mon Jan 26 08:58:05 EST 1998 | Mike McMonagle
| I have the following questions with regards to the solder printing stencil design : | 1) Is the Electro-polish process recommended for laser cut stencil ? | 2) Should the aperture walls be slanted at an angle or straight wall, i.e. trapezoidal |
Electronics Forum | Mon Feb 23 21:27:20 EST 1998 | fxb
| I have the following questions with regards to the solder printing stencil design : | 1) Is the Electro-polish process recommended for laser cut stencil ? | 2) Should the aperture walls be slanted at an angle or straight wall, i.e. trapezoidal |
Electronics Forum | Tue Jan 27 08:08:51 EST 1998 | Jon Medernach
| I have the following questions with regards to the solder printing stencil design : | 1) Is the Electro-polish process recommended for laser cut stencil ? | 2) Should the aperture walls be slanted at an angle or straight wall, i.e. trapezoidal |
Electronics Forum | Wed Oct 25 06:14:14 EDT 2000 | Adam
Guys A question regarding design rules of a WSC.We are currently running a high volume product, and as usual the design layout is as such where half the through hole connectors are perpendicular to the wave, and surprise,surpise the other half are'n