One of my customer asking me about my capability on soldering nickel strip onto the PCB pad. Given the size of the pad of 80 mil X 80 mil, and he want to ensure that we can pass 4.5kg peel force(solder wire Sn63/Pb37). Anybody with this experience ?
Electronics Forum | Tue Apr 22 12:33:35 EDT 2014 | barryg
No we have a battery spring that is soldered directly to a PCB (standard tin plated copper PCB). The Battery spring supplier (and I have no confirmation he makes them or buys them) claims they are tin plated. When trying to solder to them it is very
Electronics Forum | Mon Apr 21 16:38:45 EDT 2014 | barryg
Hello all. We have been having some problems soldering to what we believe is a nickel plated spring steel battery terminal to a PCB. We have tried scrapping , then tinning, dipping and still have problems. Are there any special fluxes or pre-treats t
Electronics Forum | Thu Nov 22 07:21:36 EST 2018 | mermarinc
Hey!Thanks for sharing.
Electronics Forum | Fri Nov 16 07:55:17 EST 2018 | robl
Hi Prem, We used to place millions of Nickel battery tabs using Cobar paste. We found it particularly aggressive. Just contact your local Cobar distributor and ask them for samples of their most aggressive fluxed paste. Kind regards, Rob.
Electronics Forum | Wed Nov 21 05:57:30 EST 2018 | premkumar_haribabu
Hi Robl, Thanks for your qucik reply!! , i understand if we use aggresive flux that we can impove solder wetting over nickel plate vs PCB pads & we need to solder through 12 zones reflow oven. Prem
Electronics Forum | Fri Nov 16 09:04:40 EST 2018 | robl
and here.... https://smtnet.com/Forums/index.cfm?fuseaction=view_thread&CFApp=1&Thread_ID=9389Message37375 Which was in the days of leaded, but the ROHS paste had the same flux formulation.
Electronics Forum | Fri Nov 16 08:41:34 EST 2018 | davef
Here's a similar thread earlier in SMTnet FORUM -- Soldering to a nickel plated battery terminal [ https://smtnet.com/Forums/index.cfm?fuseaction=view_thread&CFApp=1&Thread_ID=17474Message71990 ] We still have our neighborhood Batteries+ attach so
Electronics Forum | Mon Nov 26 13:40:40 EST 2018 | robl
Hi Prem, Yes, the flux in the Cobar paste helped with wetting and joint strength, as does reducing voids as there is more solder in the joint, as does cooling rate. Regarding peel test in KG, it depends on the pad size and volume of solder in the j
Electronics Forum | Wed Nov 21 06:07:20 EST 2018 | robl
Hi Prem, Voiding has lots of causes, but boiling off flux to quickly really doesn't help, so maybe a more gentle profile. Also you do not need to print a solid block of paste, you can print a window pain style pad to help the flux escape. Also, th
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830