problem: Too many solvents and boards are not clean Flux remains on the board after vapor degreaser and "Powdery" white residue after vapor degreasing Flux type is kester 186 Process: hand solder High Temp alloy, spot clean after hand solder e
Electronics Forum | Tue Aug 21 08:44:48 EDT 2001 | caldon
A) The standoff height of some uBGA components does not allow water to penatrate under the component. B)Water soluable may dilute the flux and not remove it all together. This can be tested with Ion Chromatography. C) Water soluable in some cases ne
Electronics Forum | Thu Feb 13 03:49:15 EST 2014 | jlawson
Yes all above is correct, as solder deposits get smaller and mesh T4+ , actual metal to air contact surface area increases , say in contrast to T3, add to this less flux , and flux running away from the joint, re-oxidation and what flux is left, can