Electronics Forum | Thu Jun 08 07:56:34 EDT 2017 | jkitt84
In an excellent previous thread davef mentions brass should be plated prior to soldering to prevent zinc leaching from the brass. It is reported once the zinc leaches, the joint is weak. He recommends copper or nickel plating. Would silver plating w
Electronics Forum | Thu Sep 24 14:23:53 EDT 1998 | Cunli Jia @ SMTnet
Dave, Greg, and All, Thank you for the comment. As you know, we do think we are the best and we owe our reputation to you, our visitors. We will continue to improve the site with more features and ease of use. One thing is for sure, we can always
Electronics Forum | Mon Dec 01 12:39:06 EST 2008 | tsvetan
this is really nice one ;) paper and cotton have lowest potential to generate static electricity see below, and usually is good practice to wear cotton glowe at least to one of your hands to not leave greasy finger spots on the gold finish of the PC
Electronics Forum | Mon Oct 09 10:00:15 EDT 2006 | C.K. the Flip
I had a customer like this too. Originally, the customer print called for manual soldering of the RF shield (which took us about 20 min. per shield to hand solder), but I changed it to Solder Reflow (I cut apertures on the stencil), with brass weigh
Electronics Forum | Sat Jul 17 03:02:58 EDT 1999 | Jeff Sanchez
| | | | | I need a good chemical to remove the lacquer finish off of magnet wire. I know there are different kinds but I need one that really works. Any suggestions would be great. thanks in advance guys. | | | | | | | | | What is it you're trying t
Electronics Forum | Sat Jul 17 13:25:02 EDT 1999 | Scott
| | | | | | I need a good chemical to remove the lacquer finish off of magnet wire. I know there are different kinds but I need one that really works. Any suggestions would be great. thanks in advance guys. | | | | | | | | | | | What is it you're tr
1 |